This work provides the first demonstration of vertical GaN Junction Barrier Schottky (JBS) rectifiers fabricated by etch and regrowth of p-GaN. A reverse blocking voltage near 1500 V was achieved at 1 mA reverse leakage, with a sub 1 V turn-on and a specific on-resistance of 10 mΩ-cm2. This result is compared to other reported JBS devices in the literature and our device demonstrates the lowest leakage slope at high reverse bias. A large initial leakage current is present near zero-bias which is attributed to a combination of inadequate etch-damage removal and passivation induced leakage current.
Ebrish, Mona A.; Anderson, Travis J.; Koehler, Andrew D.; Foster, Geoffrey M.; Gallagher, James C.; Kaplar, Robert K.; Gunning, Brendan P.; Hobart, Karl D.
GaN is a favorable martial for future efficient high voltage power switches. GaN has not dominated the power electronics market due to immature substrate, homoepitaxial growth, and immature processing technology. Understanding the impact of the substrate and homoepitaxial growth on the device performance is crucial for boosting the performance of GaN. In this work, we studied vertical GaN PiN diodes that were fabricated on non-homogenous Hydride Vapor Phase Epitaxy (HVPE) substrates from two different vendors. We show that defects which stemmed from growth techniques manifest themselves as leakage hubs. Different non-homogenous substrates showed different distribution of those defects spatially with the lesser quality substrates clustering those defects in clusters that causes pre-mature breakdown. Energetically these defects are mostly mid-gap around 1.8Ev with light emission spans from 450nm to 700nm. Photon emission spectrometry and hyperspectral electroluminescence were used to locate these defects spatially and energetically.
Optimized designs were achieved using a genetic algorithm to evaluate multi-objective trade space, including Mean-Time-Between-Failure (MTBF) and volumetric power density. This work provides a foundational platform that can be used to optimize additional power converters, such as an inverter for the EV traction drive system as well as trade-offs in thermal management due to the use of different device substrate materials.
Researchers have been extensively studying wide-bandgap (WBG) semiconductor materials such as gallium nitride (GaN) with an aim to accomplish an improvement in size, weight, and power of power electronics beyond current devices based on silicon (Si). However, the increased operating power densities and reduced areal footprints of WBG device technologies result in significant levels of self-heating that can ultimately restrict device operation through performance degradation, reliability issues, and failure. Typically, self-heating in WBG devices is studied using a single measurement technique while operating the device under steady-state direct current measurement conditions. However, for switching applications, this steady-state thermal characterization may lose significance since the high power dissipation occurs during fast transient switching events. Therefore, it can be useful to probe the WBG devices under transient measurement conditions in order to better understand the thermal dynamics of these systems in practical applications. In this work, the transient thermal dynamics of an AlGaN/GaN high electron mobility transistor (HEMT) were studied using thermoreflectance thermal imaging and Raman thermometry. Also, the proper use of iterative pulsed measurement schemes such as thermoreflectance thermal imaging to determine the steady-state operating temperature of devices is discussed. These studies are followed with subsequent transient thermal characterization to accurately probe the self-heating from steady-state down to submicrosecond pulse conditions using both thermoreflectance thermal imaging and Raman thermometry with temporal resolutions down to 15 ns.
Proper edge termination is required to reach large blocking voltages in vertical power devices. Limitations in selective area p-type doping in GaN restrict the types of structures that can be used for this purpose. A junction termination extension (JTE) can be employed to reduce field crowding at the junction periphery where the charge in the JTE is designed to sink the critical electric field lines at breakdown. One practical way to fabricate this structure in GaN is by a step-etched single-zone or multi-zone JTE where the etch depths and doping levels are used to control the charge in the JTE. The multi-zone JTE is beneficial for increasing the process window and allowing for more variability in parameter changes while still maintaining a designed percentage of the ideal breakdown voltage. Impact ionization parameters reported in literature for GaN are compared in a simulation study to ascertain the dependence on breakdown performance. Two 3-zone JTE designs utilizing different impact ionization coefficients are compared. Simulations confirm that the choice of impact ionization parameters affects both the predicted breakdown of the device as well as the fabrication process variation tolerance for a multi-zone JTE. Regardless of the impact ionization coefficients utilized, a step-etched JTE has the potential to provide an efficient, controllable edge termination design.