The Proton-21 Laboratory in the Ukraine has been publishing results on shock-induced transmutation of several elements, including Cobalt 60 into non-radioactive elements. This report documents exploratory characterization of a shock-compressed Aluminum-6061 sample, which is the only available surrogate for the high-purity copper samples in the Proton-21 experiments. The goal was to determine Sandia's ability to detect possible shock-wave-induced transmutation products and to unambiguously validate or invalidate the claims in collaboration with the Proton-21 Laboratory. We have developed a suitable characterization process and tested it on the surrogate sample. Using trace elemental analysis capabilities, we found elevated and localized concentrations of impurity elements like the Ukrainians report. All our results, however, are consistent with the ejection of impurities that were not in solution in our alloy or were deposited from the cathode during irradiation or possibly storage. Based on the detection capabilities demonstrated and additional techniques available, we are positioned to test samples from Proton-21 if funded to do so.
A method to measure interfacial mechanical properties at high temperatures and in a controlled atmosphere has been developed to study anodized aluminum surface coatings at temperatures where the interior aluminum alloy is molten. This is the first time that the coating strength has been studied under these conditions. We have investigated the effects of ambient atmosphere, temperature, and surface finish on coating strength for samples of aluminum alloy 7075. Surprisingly, the effective Young's modulus or strength of the coating when tested in air was twice as high as when samples were tested in an inert nitrogen or argon atmosphere. Additionally, the effective Young's modulus of the anodized coating increased with temperature in an air atmosphere but was independent of temperature in an inert atmosphere. The effect of surface finish was also examined. Sandblasting the surface prior to anodization was found to increase the strength of the anodized coating with the greatest enhancement noted for a nitrogen atmosphere. Machining marks were not found to significantly affect the strength.
The stainless steel alloy 17-4PH contains a martensitic microstructure and second phase delta ({delta}) ferrite. Strengthening of 17-4PH is attributed to Cu-rich precipitates produced during age hardening treatments at 900-1150 F (H900-H1150). For wrought 17-4PH, the effects of heat treatment and microstructure on mechanical properties are well-documented [for example, Ref. 1]. Fewer studies are available on cast 17-4PH, although it has been a popular casting alloy for high strength applications where moderate corrosion resistance is needed. Microstructural features and defects particular to castings may have adverse effects on properties, especially when the alloy is heat treated to high strength. The objective of this work was to outline the effects of microstructural features specific to castings, such as shrinkage/solidification porosity, on the mechanical behavior of investment cast 17-4PH. Besides heat treatment effects, the results of metallography and SEM studies showed that the largest effect on mechanical properties is from shrinkage/solidification porosity. Figure 1a shows stress-strain curves obtained from samples machined from castings in the H925 condition. The strength levels were fairly similar but the ductility varied significantly. Figure 1b shows an example of porosity on a fracture surface from a room-temperature, quasi-static tensile test. The rounded features represent the surfaces of dendrites which did not fuse or only partially fused together during solidification. Some evidence of local areas of fracture is found on some dendrite surfaces. The shrinkage pores are due to inadequate backfilling of liquid metal and simultaneous solidification shrinkage during casting. A summary of percent elongation results is displayed in Figure 2a. It was found that higher amounts of porosity generally result in lower ductility. Note that the porosity content was measured on the fracture surfaces. The results are qualitatively similar to those found by Gokhale et al. and Surappa et al. in cast A356 Al and by Gokhale et al. for a cast Mg alloys. The quantitative fractography and metallography work by Gokhale et al. illustrated the strong preference for fracture in regions of porosity in cast material. That is, the fracture process is not correlated to the average microstructure in the material but is related to the extremes in microstructure (local regions of high void content). In the present study, image analysis on random cross-sections of several heats indicated an overall porosity content of 0.03%. In contrast, the area % porosity was as high as 16% when measured on fracture surfaces of tensile specimens using stereology techniques. The results confirm that the fracture properties of cast 17-4PH cannot be predicted based on the overall 'average' porosity content in the castings.
Low temperature, Sn-based Pb-free solders were developed by making alloy additions to the starting material, 96.5Sn-3.5Ag (mass%). The melting behavior was determined using Differential Scanning Calorimetry (DSC). The solder microstructure was evaluated by optical microscopy and electron probe microanalysis (EPMA). Shear strength measurements, hardness tests, intermetallic compound (IMC) layer growth measurements, and solderability tests were performed on selected alloys. Three promising ternary alloy compositions and respective solidus temperatures were: 91.84Sn-3.33Ag-4.83Bi, 212 C; 87.5Sn-7.5Au-5.0Bi, 200 C; and 86.4Sn-5.1 Ag-8.5Au, 205 C. A quaternary alloy had the composition 86.8Sn-3.2Ag-5.0Bi-5.0Au and solidus temperature of 194 C The shear strength of this quaternary alloy was nearly twice that of the eutectic Sn-Pb solder. The 66Sn-5.0Ag-10Bi-5.0Au-101n-4.0Cu alloy had a solidus temperature of 178 C and good solderability on Cu. The lowest solidus temperature of 159 C was realized with the alloy 62Sn-5.0Ag-10Bi-4.0Au-101n-4.0Cu-5.0Ga. The contributing factor towards the melting point depression was the composition of the solid solution, Sn-based matrix phase of each solder.