We present the results of a three year LDRD project that focused on understanding the impact of defects on the electrical, optical and thermal properties of GaN-based nanowires (NWs). We describe the development and application of a host of experimental techniques to quantify and understand the physics of defects and thermal transport in GaN NWs. We also present the development of analytical models and computational studies of thermal conductivity in GaN NWs. Finally, we present an atomistic model for GaN NW electrical breakdown supported with experimental evidence. GaN-based nanowires are attractive for applications requiring compact, high-current density devices such as ultraviolet laser arrays. Understanding GaN nanowire failure at high-current density is crucial to developing nanowire (NW) devices. Nanowire device failure is likely more complex than thin film due to the prominence of surface effects and enhanced interaction among point defects. Understanding the impact of surfaces and point defects on nanowire thermal and electrical transport is the first step toward rational control and mitigation of device failure mechanisms. However, investigating defects in GaN NWs is extremely challenging because conventional defect spectroscopy techniques are unsuitable for wide-bandgap nanostructures. To understand NW breakdown, the influence of pre-existing and emergent defects during high current stress on NW properties will be investigated. Acute sensitivity of NW thermal conductivity to point-defect density is expected due to the lack of threading dislocation (TD) gettering sites, and enhanced phonon-surface scattering further inhibits thermal transport. Excess defect creation during Joule heating could further degrade thermal conductivity, producing a viscous cycle culminating in catastrophic breakdown. To investigate these issues, a unique combination of electron microscopy, scanning luminescence and photoconductivity implemented at the nanoscale will be used in concert with sophisticated molecular-dynamics calculations of surface and defect-mediated NW thermal transport. This proposal seeks to elucidate long standing material science questions for GaN while addressing issues critical to realizing reliable GaN NW devices.
Nanowires based on the III nitride materials system have attracted attention as potential nanoscale building blocks in optoelectronics, sensing, and electronics. However, before such applications can be realized, several challenges exist in the areas of controlled and ordered nanowire synthesis, fabrication of advanced nanowire heterostructures, and understanding and controlling the nanowire electrical and optical properties. Here, recent work is presented involving the aligned growth of GaN and III-nitride core-shell nanowires, along with extensive results providing insights into the nanowire properties obtained using advanced electrical, optical and structural characterization techniques.
The fundamental spontaneous emission rate for a photon source can be modified by placing the emitter inside a periodic dielectric structure allowing the emission to be dramatically enhanced or suppressed depending on the intended application. We have investigated the relatively unexplored realm of interaction between semiconductor emitters and three dimensional photonic crystals in the visible spectrum. Although this interaction has been investigated at longer wavelengths, very little work has been done in the visible spectrum. During the course of this LDRD, we have fabricated TiO{sub 2} logpile photonic crystal structures with the shortest wavelength band gap ever demonstrated. A variety of different emitters with emission between 365 nm and 700 nm were incorporated into photonic crystal structures. Time-integrated and time-resolved photoluminescence measurements were performed to measure changes to the spontaneous emission rate. Both enhanced and suppressed emission were demonstrated and attributed to changes to the photonic density of states.
The III-nitride (AlGaInN) materials system forms the foundation for white solid-state lighting, the adoption of which could significantly reduce U.S. energy needs. While the growth of GaN-based devices relies on heteroepitaxy on foreign substrates, the heteroepitaxial layers possess a high density of dislocations due to poor lattice and thermal expansion match. These high dislocation densities have been correlated with reduced internal quantum efficiency and lifetimes for GaN-based LEDs. Here, we demonstrate an inexpensive method for dislocation reduction in GaN grown on sapphire and silicon substrates. This technique, which requires no lithographic patterning, GaN is selectively grown through self-assembled layers of silica microspheres which act to filter out dislocations. Using this method, the threading dislocation density for GaN on sapphire was reduced from 3.3 x 10{sup 9} cm{sup -2} to 4.0 x 10{sup 7} cm{sup -2}, and from the 10{sup 10} cm{sup -2} range to {approx}6.0 x 10{sup 7} cm{sup -2} for GaN on Si(111). This large reduction in dislocation density is attributed to a dislocation blocking and bending by the unique interface between GaN and silica microspheres.
The proposed work seeks to demonstrate and understand new phenomena in novel, freestanding III-nitride core-shell nanowires, including 1D and 2D electron gas formation and properties, and to investigate the role of surfaces and heterointerfaces on the transport and optical properties of nanowires, using a combined experimental and theoretical approach. Obtaining an understanding of these phenomena will be a critical step that will allow development of novel, ultrafast and ultraefficient nanowire-based electronic and photonic devices.