Publications

Abstract not provided.

This SAND report is the final report on Sandia's Grand Challenge LDRD Project 27328, 'A Revolution in Lighting -- Building the Science and Technology Base for Ultra-Efficient Solid-state Lighting.' This project, which for brevity we refer to as the SSL GCLDRD, is considered one of Sandia's most successful GCLDRDs. As a result, this report reviews not only technical highlights, but also the genesis of the idea for Solid-state Lighting (SSL), the initiation of the SSL GCLDRD, and the goals, scope, success metrics, and evolution of the SSL GCLDRD over the course of its life. One way in which the SSL GCLDRD was different from other GCLDRDs was that it coincided with a larger effort by the SSL community - primarily industrial companies investing in SSL, but also universities, trade organizations, and other Department of Energy (DOE) national laboratories - to support a national initiative in SSL R&D. Sandia was a major player in publicizing the tremendous energy savings potential of SSL, and in helping to develop, unify and support community consensus for such an initiative. Hence, our activities in this area, discussed in Chapter 6, were substantial: white papers; SSL technology workshops and roadmaps; support for the Optoelectronics Industry Development Association (OIDA), DOE and Senator Bingaman's office; extensive public relations and media activities; and a worldwide SSL community website. Many science and technology advances and breakthroughs were also enabled under this GCLDRD, resulting in: 55 publications; 124 presentations; 10 book chapters and reports; 5 U.S. patent applications including 1 already issued; and 14 patent disclosures not yet applied for. Twenty-six invited talks were given, at prestigious venues such as the American Physical Society Meeting, the Materials Research Society Meeting, the AVS International Symposium, and the Electrochemical Society Meeting. This report contains a summary of these science and technology advances and breakthroughs, with Chapters 1-5 devoted to the five technical task areas: 1 Fundamental Materials Physics; 2 111-Nitride Growth Chemistry and Substrate Physics; 3 111-Nitride MOCVD Reactor Design and In-Situ Monitoring; 4 Advanced Light-Emitting Devices; and 5 Phosphors and Encapsulants. Chapter 7 (Appendix A) contains a listing of publications, presentations, and patents. Finally, the SSL GCLDRD resulted in numerous actual and pending follow-on programs for Sandia, including multiple grants from DOE and the Defense Advanced Research Projects Agency (DARPA), and Cooperative Research and Development Agreements (CRADAs) with SSL companies. Many of these follow-on programs arose out of contacts developed through our External Advisory Committee (EAC). In h s and other ways, the EAC played a very important role. Chapter 8 (Appendix B) contains the full (unedited) text of the EAC reviews that were held periodically during the course of the project.

Abstract not provided.

Photoluminescence (PL) spectroscopy was carried out on a series of Si-doped bulk InGaN films in the low indium (In) composition regime. Room temperature PL showed a factor of 25 increase in integrated intensity as the In composition was increased from 0 to 0.07. Temperature dependent PL data was fit to an Arrhenius equation to reveal an increasing activation energy for thermal quenching of the PL intensity as the In composition is increased. Time resolved PL measurements revealed that only the sample with highest In ( x=0.07) showed a strong spectral variation in decay time across the T=4K PL resonance, indicative of recombination from localized states at low temperatures. The decay times at room temperature were non-radiatively dominated for all films, and the room temperature (non-radiative) decay times increased with increasing In, from 50-230 psec for x=0-0.07. Our data demonstrate that non-radiative recombination is less effective with increasing In composition. © 2000 Materials Research Society.

Abstract not provided.

Optically pumped near ultraviolet vertical cavity laser operation (VCSEL) has been obtained under quasi-continuous wave conditions at room temperature near 383 nm from shallow InGaN/GaN multiple quantum wells (MQWs). Low loss optical resonators were fabricated by using in-situ grown (Al,Ga)N distributed Bragg reflectors that featured strain engineering design for high optical morphology, in combination with low-loss dielectric multilayer mirrors.

We demonstrate that the insertion of low-temperature (LT) AlGaN interlayers is effective in reducing mismatch-induced tensile stress and suppressing the formation of cracks during growth of AlGaN directly upon GaN epilayers., Stress evolution and relaxation is monitored using an in-situ optical stress sensor. The combination of in-situ and ex-situ. characterization techniques enables us to determine the degree of pseudomorphism in the interlayers. It is observed that the elastic tensile mismatch between AlGaN and GaN is mediated by the relaxation of interlayers; the use of interlayers offers tunability in the in-plane lattice parameters.

We report the growth and characterization of quaternary AlGaInN. A combination of photoluminescence (PL), high-resolution x-ray diffraction (XRD), and Rutherford backscattering spectrometry (RBS) characterizations enables us to explore the contours of constant PL peak energy and lattice parameter as functions of the quaternary compositions. The observation of room temperature PL emission at 351nm (with 20% Al and 5% In) renders initial evidence that the quaternary could be used to provide confinement for GaInN (and possibly GaN). AlGaInN/GrdnN MQW heterostructures have been grown; both XRD and PL measurements suggest the possibility of incorporating this quaternary into optoelectronic devices.

In this paper, we overview several of the critical materials growth, design and performance issues for nitride-based UV (<400 nm) LEDs. The critical issue of optical efficiency is presented through temperature-dependent photoluminescence studies of various UV active regions. These studies demonstrate enhanced optical efficiencies for active regions with In-containing alloys (InGaN, AlInGaN). We discuss the trade-off between the challenging growth of high Al containing alloys (AlGaN, AlGaInN), and the need for sufficient carrier confinement in UV heterostructures. Carrier leakage for various composition AlGaN barriers is examined through a calculation of the total unconfined carrier density in the quantum well system. We compare the performance of two distinct UV LED structures: GaN/AlGaN quantum well LEDs for λ<360 nm emission, and InGaN/AlGaInN quantum well LEDs for 370 nm<λ<390 nm emission.