Publications

Abstract not provided.

We are investigating the use of face-to-face porphyrin (FTF) materials as potential oxygen reduction catalysts in fuel cells. The FTF materials were popularized by Anson and Collman, and have the interesting property that varying the spacing between the porphyrin rings changes the chemistry they catalyze from a two-electron reduction of oxygen to a four-electron reduction of oxygen. Our goal is to understand how changes in the structure of the FTF materials lead to either two-electron or four-electron reductions. This understand of the FTF catalysis is important because of the potential use of these materials as fuel cell electrocatalysts. Furthermore, the laccase family of enzymes, which has been proposed as an electrocatalytic enzyme in biofuel cell applications, also has family members that display either two-electron or four electron reduction of oxygen, and we believe that an understanding of the structure-function relationships in the FTF materials may lead to an understanding of the behavior of laccase and other enzymes. We will report the results of B3LYP density functional theory studies with implicit solvent models of the reduction of oxygen in several members of the cobalt FTF family.

Exploration of the fundamental chemical behavior of the AlCl{sub 3}/SO{sub 2}Cl{sub 2} catholyte system for the ARDEC Self-Destruct Fuze Reserve Battery Project under accelerated aging conditions was completed using a variety of analytical tools. Four different molecular species were identified in this solution, three of which are major. The relative concentrations of the molecular species formed were found to depend on aging time, initial concentrations, and storage temperature, with each variable affecting the kinetics and thermodynamics of this complex reaction system. We also evaluated the effect of water on the system, and determined that it does not play a role in dictating the observed molecular species present in solution. The first Al-containing species formed was identified as the dimer [Al({mu}-Cl)Cl{sub 2}]{sub 2}, and was found to be in equilibrium with the monomer, AlCl{sub 3}. The second species formed in the reaction scheme was identified by single crystal X-ray diffraction studies as [Cl{sub 2}Al({mu}-O{sub 2}SCl)]{sub 2} (I), a scrambled AlCl{sub 3}{center_dot}SO{sub 2} adduct. The SO{sub 2}(g) present, as well as CL{sub 2}(g), was formed through decomposition of SO{sub 2}CL{sub 2}. The SO{sub 2}(g) generated was readily consumed by AlCl{sub 3} to form the adduct 1 which was experimentally verified when 1 was also isolated from the reaction of SO{sub 2}(g) and AlCl {sub 3}. The third species found was tentatively identified as a compound having the general formula {l_brace}[Al(O)Cl{sub 2}][OSCl{sub 2}]{r_brace}{sub n}. This was based on {sup 27}Al NMR data that revealed a species with tetrahedrally coordinated Al metal centers with increased oxygen coordination and the fact that the precipitate, or gel, that forms over time was shown by Raman spectroscopic studies to possess a component that is consistent with SOCl{sub 2}. The precursor to the precipitate should have similar constituents, thus the assignment of {l_brace}[Al(O)Cl{sub 2}][OSCl{sub 2}]{r_brace}{sub n}. The precipitate was further identified by solid state {sup 27}Al MAS NMR data to possess predominantly octahedral A1 metal center which implies {l_brace}[Al(O)Cl{sub 2}][OSCl{sub 2}]{r_brace}{sub n} must undergo some internal rearrangements. A reaction sequence has been proposed to account for the various molecular species identified in this complex reaction mixture during the aging process. The metallurgical welds were of high quality. These results were all visually determined there was no mechanical testing performed. However, it is recommended that the end plate geometry and weld be changed. If the present weld strength, based on .003' - .005' penetration, is sufficient for unit performance, the end plate thickness can be reduced to .005' instead of the .020' thickness. This will enable the plug to be stamped so that it can form a cap rather than a plug and solve existing problems and increase the amount of catholyte which may be beneficial to battery performance.

In situ neutron diffraction analysis was employed to study the behavior of the cathode and anode materials in a commercial Li-ion cell (Saehan Enertech, Inc) using the exact configuration of the commercial product. Accurate lattice parameters were refined for the LiCoO2 type cathode based on measurements collected as a function of the state of charge, Simultaneous structural characterization was possible on the graphitic anode as well. The simultaneous direct correlation of structural information for both the anode and cathode with the electrochemical data provided a highly detailed picture of the behavior of the active cell materials that ultimately underlie the cell performance. © 2003 The Electrochemical Society. All rights reserved.

The design, fabrication, and performance of a planar microbattery made from a silicon wafer with a bonded lid are presented. The battery is designed with two compartments, separated by four columns of micro-posts. These posts are 3 or 5 micrometers in diameter. The posts permit transport of liquid electrolyte, but stop particles of battery material from each compartment from mixing. The anode and cathode battery compartments, the posts, fill holes, and conductive vias are all made using high-aspect-ratio reactive ion (Bosch) etching. After the silicon wafer is completed, it is anodically bonded or adhesive bonded to a Pyrex{reg_sign} wafer lid. The battery materials are made from micro-disperse particles that are 3-5 micrometers in diameter. The lithium-ion chemistry is microcarbon mesobeads and lithium cobalt oxide. The battery capacity is 1.83 micro-amp-hrs/cm{sup 2} at a discharge rate of 25 microamps.

We have undertaken the synthesis of a thin film ''All Ceramic Battery'' (ACB) using solution route processes. Based on the literature and experimental results, we selected SnO{sub 2}, LiCoO{sub 2}, and LiLaTiO{sub 3} (LLT) as the anode, cathode, and electrolyte, respectively. Strain induced by lattice mismatch between the cathode and bottom electrode, as estimated by computational calculations, indicate that thin film orientations for batteries when thicknesses are as low as 500 {angstrom} are strongly controlled by surface energies. Therefore, we chose platinized silicon as the basal platform based on our previous experience with this material. The anode thin films were generated by standard spin-cast methods and processing using a solution of [Sn(ONep)]{sub 8} and HOAc which was found to form Sn{sub 6}(O){sub 4}(ONep){sub 4}. Electrochemical evaluation showed that the SnO{sub 2} was converted to Sn{sup o} during the first cycle. The cathode was also prepared by spin coating using the novel [Li(ONep)]{sub 8} and Co(OAc){sub 2}. The films could be electrochemically cycled (i.e., charged/discharged), with all of the associated structural changes being observable by XRD. Computational models indicated that the LLT electrolyte would be the best available ceramic material for use as the electrolyte. The LLT was synthesized from [Li(ONep)]{sub 8}, [Ti(ONep){sub 4}]{sub 2}, and La(DIP){sub 3}(py){sub 3} with RTP processing at 900 C being necessary to form the perovskite phase. Alternatively, a novel route to thin films of the block co-polymer ORMOLYTE was developed. The integration of these components was undertaken with each part of the assembly being identifiably by XRD analysis (this will allow us to follow the progress of the charge/discharge cycles of the battery during use). SEM investigations revealed the films were continuous with minimal mixing. All initial testing of the thin-film cathode/electrolyte/anode ACB devices revealed electrical shorting. Alternative approaches for preparing non-shorted devices (e.g. inverted and side-by-side) are under study.

Abstract not provided.

Electrical and chemical measurements have been made on 18650-size lithium-ion cells that have been exposed to calendar and cycle life aging at temperatures up to 70 C. Aging times ranged from 2 weeks at the highest temperature to several months under more moderate conditions. After aging, the impedance behavior of the cells was reversed from that found originally, with lower impedance at low state of charge and the total impedance was significantly increased. Investigations using a reference electrode showed that these changes are primarily due to the behavior of the cathode. Measurements of cell impedance as a function of cell voltage reveal a pronounced minimum in the total impedance at approximately 40--50% state-of-charge (SOC). Chemical analysis data are presented to support the SOC assignments for aged and unaged cells. Electrochemical impedance spectroscopy (EIS) data have been recorded at several intermediate states of charge to construct the impedance vs. open circuit voltage curve for the cell. This information has not previously been available for the LiNi{sub 0.85}Co{sub 0.15}O{sub 2} cathode material. Structural and chemical analysis information obtained from cell components removed during postmortems will also be discussed in order to reveal the true state of charge of the cathode and to develop a more complete lithium inventory for the cell.