Here we investigated the microstructural response of various Pd physically vapor deposited films and Er and ErD₂ samples prepared from neutron Tube targets to implanted He via in situ ion irradiation transmission electron microscopy and subsequent in situ annealing experiments. Small bubbles formed in both systems during implantation, but did not grow with increasing fluence or a short duration room temperature aging (weeks). Annealing produced large cavities with different densities in the two systems. The ErD₂ showed increased cavity nucleation compared to Er. The spherical bubbles formed from high fluence implantation and rapid annealing in both Er and ErD₂ cases differed from microstructures of naturally aged tritiated samples. Further work is still underway to determine the transition in bubble shape in the Er samples, as well as the mechanism for evolution in Pd films.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Erbium is known to effectively load with hydrogen when held at high temperature in a hydrogen atmosphere. To make the storage of hydrogen kinetically feasible, a thermal activation step is required. Activation is a routine practice, but very little is known about the physical, chemical, and/or electronic processes that occur during Activation. This work presents in situ characterization of erbium Activation using variable energy photoelectron spectroscopy at various stages of the Activation process. Modification of the passive surface oxide plays a significant role in Activation. The chemical and electronic changes observed from core-level and valence band spectra will be discussed along with corroborating ion scattering spectroscopy measurements.

Erbium is known to effectively load with hydrogen when held at high temperature in a hydrogen atmosphere. To make the storage of hydrogen kinetically feasible, a thermal activation step is required. Activation is a routine practice, but very little is known about the physical, chemical, and/or electronic processes that occur during Activation. This work presents in situ characterization of erbium Activation using variable energy photoelectron spectroscopy at various stages of the Activation process. Modification of the passive surface oxide plays a significant role in Activation. The chemical and electronic changes observed from core-level and valence band spectra will be discussed along with corroborating ion scattering spectroscopy measurements.

In an effort to better understand the structural changes occurring during hydrogen loading of erbium target materials, we have performed in situ D{sub 2} loading of erbium metal (powder) at temperature (450 C) with simultaneous neutron diffraction analysis. This experiment tracked the conversion of Er metal to the {alpha} erbium deuteride (solid-solution) phase and then into the {beta} (fluorite) phase. Complete conversion to ErD{sub 2.0} was accomplished at 10 Torr D{sub 2} pressure with deuterium fully occupying the tetrahedral sites in the fluorite lattice.

Erbium metal thin-films have been deposited on molybdenum-on-silicon substrates and then converted to erbium dideuteride (ErD2). Here, we study the effects of deposition temperature (≈300 or 723 K) and deposition rate (1 or 20 nm/s) upon the initial Er metal microstructure and subsequent ErD2 microstructure. We find that low deposition temperature and low deposition rate lead to small Er metal grain sizes, and high deposition temperature and deposition rate led to larger Er metal grain sizes, consistent with published models of metal thin-film growth. ErD2 grain sizes are strongly influenced by the prior-metal grain size, with small metal grains leading to large ErD2 grains. A novel sample preparation technique for electron backscatter diffraction of air-sensitive ErD2 was developed, and allowed the quantitative measurement of ErD2 grain size and crystallographic texture. Finer-grained ErD2 showed a strong (1 1 1) fiber texture, whereas larger grained ErD2 had only weak texture. We hypothesize that this inverse correlation may arise from improved hydrogen diffusion kinetics in the more defective fine-grained metal structure or due to improved nucleation in the textured large-grain Er. © 2010 Elsevier B.V. All rights reserved.

Erbium metal thin-films have been deposited on molybdenum-on-silicon substrates and then converted to erbium dideuteride (ErD{sub 2}). Here, we study the effects of deposition temperature ({approx}300 or 723 K) and deposition rate (1 or 20 nm/s) upon the initial Er metal microstructure and subsequent ErD{sub 2} microstructure. We find that low deposition temperature and low deposition rate lead to small Er metal grain sizes, and high deposition temperature and deposition rate led to larger Er metal grain sizes, consistent with published models of metal thin-film growth. ErD{sub 2} grain sizes are strongly influenced by the prior-metal grain size, with small metal grains leading to large ErD{sub 2} grains. A novel sample preparation technique for electron backscatter diffraction of air-sensitive ErD{sub 2} was developed, and allowed the quantitative measurement of ErD{sub 2} grain size and crystallographic texture. Finer-grained ErD{sub 2} showed a strong (1 1 1) fiber texture, whereas larger grained ErD{sub 2} had only weak texture. We hypothesize that this inverse correlation may arise from improved hydrogen diffusion kinetics in the more defective fine-grained metal structure or due to improved nucleation in the textured large-grain Er.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Erbium dihydride Er(H,D,T){sub 2} is a fluorite structure rare-earth dihydride useful for the storage of hydrogen isotopes in the solid state. However, thermodynamic predictions indicate that erbium oxide formation will proceed readily during processing, which may detrimentally contaminate Er(H,D,T){sub 2} films. In this work, transmission electron microscopy (TEM) techniques including energy-dispersive x-ray spectroscopy, energy-filtered TEM, selected area electron diffraction, and high-resolution TEM are used to examine the manifestation of oxygen contamination in ErD{sub 2} thin films. An oxide layer {approx}30-130 nm thick was found on top of the underlying ErD{sub 2} film, and showed a cube-on-cube epitaxial orientation to the underlying ErD{sub 2}. Electron diffraction confirmed the oxide layer to be Er{sub 2}O{sub 3}. While the majority of the film was observed to have the expected fluorite structure for ErD{sub 2}, secondary diffraction spots suggested the possibility of either nanoscale oxide inclusions or hydrogen ordering. In situ heating experiments combined with electron diffraction ruled out the possibility of hydrogen ordering, so epitaxial oxide nanoinclusions within the ErD{sub 2} matrix are hypothesized. TEM techniques were applied to examine this oxide nanoinclusion hypothesis.