Publications

Abstract not provided.

Abstract not provided.

Abstract not provided.

Ammonothermal growth of bulk gallium nitride (GaN) crystals is considered the most suitable method to meet the demand for high quality bulk substrates for power electronics. A non-destructive evaluation of defect content in state-of-the-art ammonothermal substrates has been carried out by synchrotron X-ray topography. Using a monochromatic beam in grazing incidence geometry, high resolution X-ray topographs reveal the various dislocation types present. Ray-tracing simulations that were modified to take both surface relaxation and absorption effects into account allowed improved correlation with observed dislocation contrast so that the Burgers vectors of the dislocations could be determined. The images show the very high quality of the ammonothermal GaN substrate wafers which contain low densities of threading dislocations (TDs) but are free of basal plane dislocations (BPDs). Threading mixed dislocations (TMDs) were found to be dominant among the TDs, and the overall TD density (TDD) of a 1-inch wafer was found to be as low as 5.16 × 103 cm−2.

Steady-state photocapacitance (SSPC) was conducted on nonpolar m-plane GaN n-type Schottky diodes to evaluate the defects induced by inductively coupled plasma (ICP) dry etching in etched-and-regrown unipolar structures. An ∼10× increase in the near-midgap Ec - 1.9 eV level compared to an as-grown material was observed. Defect levels associated with regrowth without an etch were also investigated. The defects in the regrown structure (without an etch) are highly spatially localized to the regrowth interface. Subsequently, by depth profiling an etched-and-regrown sample, we show that the intensities of the defect-related SSPC features associated with dry etching depend strongly on the depth away from the regrowth interface, which is also reported previously [Nedy et al., Semicond. Sci. Technol. 30, 085019 (2015); Fang et al., Jpn. J. Appl. Phys. 42, 4207-4212 (2003); and Cao et al., IEEE Trans. Electron Devices 47, 1320-1324 (2000)]. A photoelectrochemical etching (PEC) method and a wet AZ400K treatment are also introduced to reduce the etch-induced deep levels. A significant reduction in the density of deep levels is observed in the sample that was treated with PEC etching after dry etching and prior to regrowth. An ∼2× reduction in the density of Ec - 1.9 eV level compared to a reference etched-and-regrown structure was observed upon the application of PEC etching treatment prior to the regrowth. The PEC etching method is promising for reducing defects in selective-area doping for vertical power switching structures with complex geometries [Meyers et al., J. Electron. Mater. 49, 3481-3489 (2020)].

Abstract not provided.

Abstract not provided.

Researchers have been extensively studying wide-bandgap (WBG) semiconductor materials such as gallium nitride (GaN) with an aim to accomplish an improvement in size, weight, and power of power electronics beyond current devices based on silicon (Si). However, the increased operating power densities and reduced areal footprints of WBG device technologies result in significant levels of self-heating that can ultimately restrict device operation through performance degradation, reliability issues, and failure. Typically, self-heating in WBG devices is studied using a single measurement technique while operating the device under steady-state direct current measurement conditions. However, for switching applications, this steady-state thermal characterization may lose significance since the high power dissipation occurs during fast transient switching events. Therefore, it can be useful to probe the WBG devices under transient measurement conditions in order to better understand the thermal dynamics of these systems in practical applications. In this work, the transient thermal dynamics of an AlGaN/GaN high electron mobility transistor (HEMT) were studied using thermoreflectance thermal imaging and Raman thermometry. Also, the proper use of iterative pulsed measurement schemes such as thermoreflectance thermal imaging to determine the steady-state operating temperature of devices is discussed. These studies are followed with subsequent transient thermal characterization to accurately probe the self-heating from steady-state down to submicrosecond pulse conditions using both thermoreflectance thermal imaging and Raman thermometry with temporal resolutions down to 15 ns.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Gallium nitride substrates grown by the hydride vapor phase epitaxy (HVPE) method using a patterned growth process have been characterized by synchrotron monochromatic beam X-ray topography in the grazing incidence geometry. Images reveal a starkly heterogeneous distribution of dislocations with areas as large as 0.3 mm2 containing threading dislocation densities below 103 cm−2 in between a grid of strain centers with higher threading dislocation densities (>104 cm−2). Basal plane dislocation densities in these areas are as low as 104 cm−2. By comparing the recorded images of dislocations with ray tracing simulations of expected dislocations in GaN, the Burgers vectors of the dislocations have been determined. The distribution of threading screw/mixed dislocations (TSDs/TMDs), threading edge dislocations (TEDs) and basal plane dislocations (BPDs) is discussed with implications for fabrication of power devices.

Abstract not provided.

AlGaN polarization-doped field-effect transistors were characterized by DC and pulsed measurements from room temperature to 500 °C in ambient. DC current-voltage characteristics demonstrated only a 70% reduction in on-state current from 25 to 500 °C and full gate modulation, regardless of the operating temperature. Near ideal gate lag measurement was realized across the temperature range that is indicative of a high-quality substrate and sufficient surface passivation. The ability for operation at high temperature is enabled by the high Schottky barrier height from the Ni/Au gate contact, with values of 2.05 and 2.76 eV at 25 and 500 °C, respectively. The high barrier height due to the insulatorlike aluminum nitride layer leads to an ION/IOFF ratio of 1.5 × 109 and 6 × 103 at room temperature and 500 °C, respectively. Transmission electron microscopy was used to confirm the stability of the heterostructure even after an extended high-temperature operation with only minor interdiffusion of the Ni/Au Schottky contact. The use of refractory metals in all contacts will be key to ensure a stable extended high-temperature operation.

Research results for AlGaN-channel transistors are reviewed as they have progressed from low Al-content and long-channel devices to Al-rich and short-channel RF devices. Figure of merit (FOM) analysis shows encouraging comparisons relative to today's state-of-the-art GaN devices for high Al-content and elevated temperatures. Critical electric field (EC), which fuels the AlGaN transistor FOM for high Al-composition, is not measured directly, but average gate-drain electric field at breakdown is substantially better in multiple reported AlGaN-channel devices compared to GaN. Challenges for AlGaN include the constraints arising from relatively low room temperature mobility dominated by ternary alloy scattering and the difficulty of making low-resistivity Ohmic contacts to high Al-content materials. Nevertheless, considerable progress has been made recently in the formation of low-resistivity Ohmic contacts to Al-rich AlGaN by using reverse compositional grading in the semiconductor, whereby a contact to a lower-Al alloy (or even to GaN) is made. Specific contact resistivity (ρc) approaching ρc ∼2 × 10-6ωcm2 to AlGaN devices with 70% Al-content in the channel has been reported. Along with scaling of the channel length and tailoring of the threshold voltage, this has enabled a dramatic increase in the current density, which has now reached 0.6 A/mm. Excellent ION/IOFF current ratios have been reported for Schottky-gated structures, in some cases exceeding 109. Encouraging RF performance in Al-rich transistors has been reported as well, with fT and fmax demonstrated in the tens of gigahertz range for devices with less than 150 nm gates. Al-rich transistors have also shown lesser current degradation over temperature than GaN in extreme high-temperature environments up to 500 °C, while maintaining ION/IOFF ratios of ∼106 at 500 °C. Finally, enhancement-mode devices along with initial reliability and radiation results have been reported for Al-rich AlGaN transistors. The Al-rich transistors promise to be a very broad and exciting field with much more progress expected in the coming years as this technology matures.

GaN p-n diodes were formed by selective area regrowth on freestanding GaN substrates using a dry etch, followed by post-etch surface treatment to reduce etch-induced defects, and subsequent regrowth into wells. Etched-and-regrown diodes with a 150 μm diameter achieved 840 V operation at 0.5 A/cm2 reverse current leakage and a specific on-resistance of 1.2 mΩ·cm2. Etched-and-regrown diodes were compared with planar, regrown diodes without etching on the same wafer. Both types of diodes exhibited similar forward and reverse electrical characteristics, which indicate that etch-induced defectivity of the junction was sufficiently mitigated so as not to be the primary cause for leakage. An area dependence for forward and reverse leakage current density was observed, suggesting that the mesa sidewall provided a leakage path.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Impacts of silicon, carbon, and oxygen interfacial impurities on the performance of high-voltage vertical GaN-based p–n diodes are investigated. The results indicate that moderate levels (≈5 × 10¹⁷ cm^-3) of all interfacial impurities lead to reverse blocking voltages (V_b) greater than 200 V at 1 μA cm^-2 and forward leakage of less than 1 µA cm^-2 at 1.7 V. At higher interfacial impurity levels, the performance of the diodes becomes compromised. Herein, it is concluded that each impurity has a different effect on the device performance. For example, a high carbon spike at the junction correlates with high off-state leakage current in forward bias (≈100× higher forward leakage current compared with a reference diode), whereas the reverse bias behavior is not severely affected (> 200 V at 1 μA cm^-2). High silicon and oxygen spikes at the junction strongly affect the reverse leakage currents (≈ 1–10 V at 1 μA cm^-2). Regrown diodes with impurity (silicon, oxygen, and carbon) levels below 5 × 10¹⁷ cm^-3 show comparable forward and reverse results with the reference continuously grown diodes. The effect of the regrowth interface position relative to the metallurgical junction on the diode performance is also discussed.

Abstract not provided.

Abstract not provided.

Abstract not provided.

Abstract not provided.