Microstructural Analysis of Cadmium Whiskers on Long-Term-Used Hardware

Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

White, Rachel W.; Ghanbari, Zahra G.; Susan, D.F.; Dickens, Sara D.; Ruggles, Timothy R.; Perry, Daniel L.

A survey of cadmium plated field return hardware showed ubiquitous cadmium whisker growth. The most worn and debris-covered hardware showed the densest whisker growth. Whiskers were often found growing in agglomerates of nodules and whiskers. The hardware was rinsed with alcohol to transfer whiskers and debris from the hardware to a flat stub. Fifty whiskers were studied individually by scanning electron microscopy (SEM), including energy dispersive spectroscopy (EDS) and electron backscatter diffraction (EBSD). Most of the whiskers were single crystal, though three were found to contain grain boundaries at kinks. The whiskers ranged from 5 to 600 μm in length and 80 pct showed a <1 ¯ 2 1 ¯ 0> type growth direction. This growth direction facilitates the development of low energy side faces of the whisker, (0001) and {1010}.

More Details

Microstructural modification of additively manufactured metals by electropulsing

Additive Manufacturing

Noell, Philip N.; Rodelas, Jeffrey R.; Ghanbari, Zahra G.; Laursen, Christopher M.

Additive manufacturing (AM) promises rapid development cycles and fabrication of ready-to-use, geometrically-complex parts. The metallic parts produced by AM often contain highly non-equilibrium microstructures, e.g. chemical microsegregation and residual dislocation networks. While such microstructures can enhance some material properties, they are often undesirable. Many AM parts are thus heat-treated after fabrication, a process that significantly slows production. This study investigated if electropulsing, the process of sending high-current-density electrical pulses through a metallic part, could be used to modify the microstructures of AM 316 L stainless steel (SS) and AlSi10Mg parts fabricated by selective laser melting (SLM) more rapidly than thermal annealing. Electropulsing has shown promise as a rapid postprocessing method for materials fabricated using conventional methods, e.g. casting and rolling, but has never been applied to AM materials. For both the materials used in this study, as-fabricated SLM parts contained significant chemical heterogeneity, either chemical microsegregation (316 L SS) or a cellular interdendritic phase (AlSi10Mg). In both cases, annealing times on the order of hours at high homologous temperatures are necessary for homogenization. Using electropulsing, chemical microsegregation was eliminated in 316 L SS samples after 10, 16 ms electrical pulses. In AlSi10Mg parts, electropulsing produced spheroidized Si-rich particles after as few as 15, 16 ms electrical pulses with a corresponding increase in ductility. This study demonstrated that electropulsing can be used to modify the microstructures of AM metals.

More Details

Microstructural Modification and Healing of Additively Manufactured Parts by Electropulsing

Noell, Philip N.; Rodelas, Jeffrey R.; Ghanbari, Zahra G.; Laursen, Christopher M.

For many applications, the promises of additive manufacturing (AM) of rapid development cycles and fabrication of ready-to-use, geometrically-complex parts cannot be realized because of cumbersome thermal postprocessing. This postprocessing is necessary when the non- equilibrium microstructures produced by AM lead to poor material properties. This study investigated if electropulsing, the process of sending high-current-density electrical pulses through a metallic part, could be used to modify the material properties of AM parts. This process has been used to modify conventional wrought materials but has never been applied to AM materials. Two representative AM materials were examined: 316L stainless steel and A1Si10Mg. Two hours of annealing are needed to remove chemical microsegregation in AM 316L; using electropulsing, this was accomplished in 200 seconds. The ductility of AlSil0Mg parts was increased above that of the as-built material using electropulsing. This study demonstrated that electropulsing can be used to modify the microstructures of AM metals. ACKNOWLEDGEMENTS The authors would like to acknowledge Jay Carroll for beneficial discussions and supplying material. Also, the authors would like to acknowledge Zachary Casias, Peter Duran, John Laing, Sara Dickens, Celedonio Jaramillo, Renae Hickman, and Christina Profazi for their exceptional experimental support.

More Details