Vertical gallium nitride (GaN) p-n diodes have garnered significant interest for use in power electronics where high-voltage blocking and high-power efficiency are of concern. In this article, we detail the growth and fabrication methods used to develop a large area (1 mm2) vertical GaN p-n diode capable of a 6.0-kV breakdown. We also demonstrate a large area diode with a forward pulsed current of 3.5 A, an 8.3-mΩ$\cdot$cm2 differential specific ON-resistance, and a 5.3-kV reverse breakdown. In addition, we report on a smaller area diode (0.063 mm2) that is capable of 6.4-kV breakdown with a differential specific ON-resistance of 10.2 mΩ$\cdot$cm2, when accounting for current spreading through the drift region at a 45° angle. Finally, the demonstration of avalanche breakdown is shown for a 0.063-mm2 diode with a room temperature breakdown of 5.6 kV. In this work, these results were achieved via epitaxial growth of a 50-μm drift region with a very low carrier concentration of <1×1015 cm–3 and a carefully designed four-zone junction termination extension.
GaN p-n diodes were formed by selective area regrowth on freestanding GaN substrates using a dry etch, followed by post-etch surface treatment to reduce etch-induced defects, and subsequent regrowth into wells. Etched-and-regrown diodes with a 150 μm diameter achieved 840 V operation at 0.5 A/cm2 reverse current leakage and a specific on-resistance of 1.2 mΩ·cm2. Etched-and-regrown diodes were compared with planar, regrown diodes without etching on the same wafer. Both types of diodes exhibited similar forward and reverse electrical characteristics, which indicate that etch-induced defectivity of the junction was sufficiently mitigated so as not to be the primary cause for leakage. An area dependence for forward and reverse leakage current density was observed, suggesting that the mesa sidewall provided a leakage path.
The impact of dry-etch-induced defects on the electrical performance of regrown, c-plane, GaN p-n diodes where the p-GaN layer is formed by epitaxial regrowth using metal-organic, chemical-vapor deposition was investigated. Diode leakage increased significantly for etched-and-regrown diodes compared to continuously grown diodes, suggesting a defect-mediated leakage mechanism. Deep level optical spectroscopy (DLOS) techniques were used to identify energy levels and densities of defect states to understand etch-induced damage in regrown devices. DLOS results showed the creation of an emergent, mid-gap defect state at 1.90 eV below the conduction band edge for etched-and-regrown diodes. Reduction in both the reverse leakage and the concentration of the 1.90 eV mid-gap state was achieved using a wet chemical treatment on the etched surface before regrowth, suggesting that the 1.90 eV deep level contributes to increased leakage and premature breakdown but can be mitigated with proper post-etch treatments to achieve >600 V reverse breakdown operation.
Gate length dependent (80 nm–5000 mm) radio frequency measurements to extract saturation velocity are reported for Al0.85Ga0.15N/Al0.7Ga0.3N high electron mobility transistors fabricated into radio frequency devices using electron beam lithography. Direct current characterization revealed the threshold voltage shifting positively with increasing gate length, with devices changing from depletion mode to enhancement mode when the gate length was greater than or equal to 450 nm. Transconductance varied from 10 mS/mm to 25 mS/mm, with the 450 nm device having the highest values. Maximum drain current density was 268 mA/mm at 10 V gate bias. Scattering-parameter characterization revealed a maximum unity gain bandwidth (fT) of 28 GHz, achieved by the 80 nm gate length device. A saturation velocity value of 3.8 × 106 cm/s, or 35% of the maximum saturation velocity reported for GaN, was extracted from the fT measurements.
AlGaN-channel high electron mobility transistors (HEMTs) were operated as visible- and solar-blind photodetectors by using GaN nanodots as an optically active floating gate. The effect of the floating gate was large enough to switch an HEMT from the off-state in the dark to an on-state under illumination. This opto-electronic response achieved responsivity > 108 A/W at room temperature while allowing HEMTs to be electrically biased in the offstate for low dark current and low DC power dissipation. The influence of GaN nanodot distance from the HEMT channel on the dynamic range of the photodetector was investigated, along with the responsivity and temporal response of the floating gate HEMT as a function of optical intensity. The absorption threshold was shown to be controlled by the AlN mole fraction of the HEMT channel layer, thus enabling the same device design to be tuned for either visible- or solar-blind detection.
Enhancement-mode Al0.7Ga0.3N-channel high electron mobility transistors (HEMTs) were achieved through a combination of recessed etching and fluorine ion deposition to shift the threshold voltage (VTH) relative to depletion-mode devices by +5.6 V to VTH = +0.5 V. Accounting for the threshold voltage shift (ΔVTH), current densities of approximately 30 to 35 mA/mm and transconductance values of 13 mS/mm were achieved for both the control and enhancement mode devices at gate biases of 1 V and 6.6 V, respectively. Little hysteresis was observed for all devices, with voltage offsets of 20 mV at drain currents of 1.0 × 10-3mA/mm. Enhancement-mode devices exhibited slightly higher turn-on voltages (+0.38 V) for forward bias gate currents. Piecewise evaluation of a threshold voltage model indicated a ΔVTH of +3.3 V due to a gate recess etching of 12 nm and an additional +2.3 V shift due to fluorine ions near the AlGaN surface.
Here, we present a low resistance, straightforward planar ohmic contact for Al0.45Ga0.55N/Al0.3Ga0.7N high electron mobility transistors. Five metal stacks (a/Al/b/Au; a = Ti, Zr, V, Nb/Ti; b = Ni, Mo, V) were evaluated at three individual annealing temperatures (850, 900, and 950°C). The Ti/Al/Ni/Au achieved the lowest specific contact resistance at a 900°C anneal temperature. Transmission electron microscopy analysis revealed a metal-semiconductor interface of Ti-Al-Au for an ohmic (900°C anneal) and a Schottky (850°C anneal) Ti/Al/Ni/Au stack. HEMTs were fabricated using the optimized recipe with resulting contacts that had room-temperature specific contact resistances of ρc = 2.5 × 10-5 Ω cm², sheet resistances of RSH = 3.9 kΩ/$\blacksquare$, and maximum current densities of 75 mA/mm (at VGATE of 2 V). Electrical measurements from -50 to 200°C had decreasing specific contact resistance and increasing sheet resistance, with increasing temperature. These contacts enabled state-of-the-art performance of Al0.45Ga0.55N/Al0.3Ga0.7N HEMTs.