We performed measurements and analyses of the prompt radiation-induced conductivity (RIC) in thin samples of polyurethane foam and glass microballoon foam at the Little Mountain Medusa LINAC facility in Ogden, UT. The RIC coefficient was non-linear with dose rate for polyurethane foam; however, typical values at 1E11 rad(si)/s dose rate was measured as 0.8E-11 mho/m/rad/s for 5 lb./cu ft. foam and 0.3E-11 mho/m/rad/s for 10 lb./cu ft. density polyurethane foam. For encapsulated glass microballoons (GMB) the RIC coefficient was approximately 1E-15 mho/m/rad/s and was not a strong function of dose rate.
In this report, measurements of the prompt radiation-induced conductivity (RIC) in 3 mil samples of Pyralux® are presented as a function of dose rate, pulse width, and applied bias. The experiments were conducted with the Medusa linear accelerator (LINAC) located at the Little Mountain Test Facility (LMTF) near Ogden, UT. The nominal electron energy for the LINAC is 20 MeV. Prompt conduction current data were obtained for dose rates ranging from ~2 x 109 rad(Si)/s to ~1.1 x 1011 rad(Si)/s and for nominal pulse widths of 50 ns and 500 ns. At a given dose rate, the applied bias across the samples was stepped between -1500 V and 1500 V. Calculated values of the prompt RIC varied between 1.39x10-8 Ω-1 · m-1 and 2.67x10-7 Ω-1 · m-1 and the prompt RIC coefficient varied between 1.25x10-18 Ω-1 · m-1/(rad/s) and 1.93x10-17 Ω-1 · m-1/(rad/s).
We performed measurements of the prompt radiation induced conductivity (RIC) in thin samples of Teflon (PTFE) at the Little Mountain Medusa LINAC facility in Ogden, UT. Three mil (76.2 microns) samples were irradiated with a 0.5 %CE%BCs pulse of 20 MeV electrons, yielding dose rates of 1E9 to 1E11 rad/s. We applied variable potentials up to 2 kV across the samples and measured the prompt conduction current. Details of the experimental apparatus and analysis are reported in this report on prompt RIC in Teflon.
We performed measurements of the prompt radiation induced conductivity in thin samples of Alumina and Sapphire at the Little Mountain Medusa LINAC facility in Ogden, UT. Five mil thick samples were irradiated with pulses of 20 MeV electrons, yielding dose rates of 1E7 to 1E9 rad/s. We applied variable potentials up to 1 kV across the samples and measured the prompt conduction current. Analysis rendered prompt conductivity coefficients between 1E10 and 1E9 mho/m/(rad/s), depending on the dose rate and the pulse width for Alumina and 1E7 to 6E7 mho/m/(rad/s) for Sapphire.
We performed measurements of the prompt radiation induced conductivity in thin samples of Kapton (polyimide) at the Little Mountain Medusa LINAC facility in Ogden, UT. Three mil samples were irradiated with a 0.5 {mu}s pulse of 20 MeV electrons, yielding dose rates of 1E9 to 1E10 rad/s. We applied variable potentials up to 2 kV across the samples and measured the prompt conduction current. Analysis rendered prompt conductivity coefficients between 6E-17 and 2E-16 mhos/m per rad/s, depending on the dose rate and the pulse width.
This report presents a test protocol for screening capacitors dielectrics for charge loss due to ionizing radiation. The test protocol minimizes experimental error and provides a test method that allows comparisons of different dielectric types if exposed to the same environment and if the same experimental technique is used. The test acceptance or screening method is fully described in this report. A discussion of technical issues and possible errors and uncertainties is included in this report also.
Using a differential absorption spectrometer we obtained experimental spectral information for the PITHON Flash X-ray Machine located in San Leandro, California at L-3 Communications. Spectral information we obtained pertained to the 200 keV to 800 keV endpoint operation of PITHON. We also obtained data on the temporal behavior of high energy and low energy spectral content.