Plasma formation from intensely ohmically heated conductors is known to be highly non-uniform, as local overheating can be driven by micron-scale imperfections. Detailed understanding of plasma formation is required to predict the performance of magnetically driven physics targets and magnetically-insulated transmission lines (MITLs). Previous LDRD-supported work (projects 178661 and 200269) developed the electrothermal instability (ETI) platform, on the Mykonos facility, to gather high-resolution images of the self-emission from the non-uniform ohmic heating of z-pinch rods. Experiments studying highly inhomogeneous alloyed aluminum captured complex heating topography. To enable detailed comparison with magnetohydrodynamic (MHD) simulation, 99.999% pure aluminum rods in a z-pinch configuration were diamond-turned to ~10nm surface roughness and then further machined to include well-characterized micron-scale "engineered" defects (ED) on the rod's surface (T.J. Awe, et al., Phys. Plasmas 28, 072104 (2021)). In this project, the engineered defect hardware and diagnostic platform were used to study ETI evolution and non-uniform plasma formation from stainless steel targets. The experimental objective was to clearly determine what, if any, role manufacturing, preparation, or alloy differences have in encouraging nonuniform heating and plasma formation from high-current density stainless steel. Data may identify improvements that may be implemented in the fabrication/preparation of electrodes used on the Z machine. Preliminary data shows that difference in manufacturer has no observed effect on ETI evolution, stainless alloy 304L heated more uniformly than alloy 310 at similar current densities, and that stainless steel undergoes the same evolutionary ETI stages as ultra-pure aluminum, with increased emission tied to areas of elevated surface roughness.
Although gold remains a preferred surface finish for components used in high-reliability electronics, rapid developments in this area have left a gap in the fundamental understanding of solder joint gold (Au) embrittlement. Furthermore, as electronic designs scale down in size, the effect of Au content is not well understood on increasingly smaller solder interconnections. As a result, previous findings may have limited applicability. The current study focused on addressing these gaps by investigating the interfacial microstructure that evolves in 63Sn-37Pb solder joints as a function of Au layer thickness. Those findings were correlated to the mechanical performance of the solder joints. Increasing the initial Au concentration decreased the mechanical strength of a joint, but only to a limited degree. Kirkendall voids were the primary contributor to low-strength joints, while brittle fracture within the intermetallic compounds (IMC) layers is less of a factor. The Au embrittlement mechanism appears to be self-limiting, but only once mechanical integrity is degraded. Sufficient void evolution prevents continued diffusion from the remaining Au.
The composition and phase fraction of the intergranular phase of 94ND10 ceramic is determined and fabricated ex situ. The fraction of each phase is 85.96 vol% Al2O3 bulk phase, 9.46 vol% Mg-rich intergranular phase, 4.36 vol% Ca/Si-rich intergranular phase, and 0.22 vol% voids. The Ca/Si-rich phase consists of 0.628 at% Mg, 12.59 at% Si, 10.24 at% Ca, 17.23 at% Al, and balance O. The Mgrich phase consists of 14.17 at% Mg, 0.066 at% Si, 0.047 at% Ca, 28.69 at% Al, and balance O. XRD of the ex situ intergranular material made by mixed oxides consisting of the above phase and element fractions yielded 92 vol% MgAl2O4 phase and 8 vol% CaAl2Si2O8 phase. The formation of MgAl2O4 phase is consistent with prior XRD of 94ND10, while the CaAl2Si2O8 phase may exist in 94ND10 but at a concentration not readily detected with XRD. The MgAl2O4 and CaAl2Si2O8 phases determined from XRD are expected to have the elemental compositions for the Mg-rich and Ca/Si-rich phases above by cation substitutions (e.g., some Mg substituted for by Ca in the Mg-rich phase) and impurity phases not detectable with XRD.