Some of the primary barriers to widespread adoption of metal additive manufacturing (AM) are persistent defect formation in built components, high material costs, and lack of consistency in powder feedstock. To generate more reliable, complex-shaped metal parts, it is crucial to understand how feedstock properties change with reuse and how that affects build mechanical performance. Powder particles interacting with the energy source, yet not consolidated into an AM part can undergo a range of dynamic thermal interactions, resulting in variable particle behavior if reused. In this work, we present a systematic study of 316L powder properties from the virgin state through thirty powder reuses in the laser powder bed fusion process. Thirteen powder characteristics and the resulting AM build mechanical properties were investigated for both powder states. Results show greater variability in part ductility for the virgin state. The feedstock exhibited minor changes to size distribution, bulk composition, and hardness with reuse, but significant changes to particle morphology, microstructure, magnetic properties, surface composition, and oxide thickness. Additionally, sieved powder, along with resulting fume/condensate and recoil ejecta (spatter) properties were characterized. Formation mechanisms are proposed. It was discovered that spatter leads to formation of single crystal ferrite through large degrees of supercooling and massive solidification. Ferrite content and consequently magnetic susceptibility of the powder also increases with reuse, suggesting potential for magnetic separation as a refining technique for altered feedstock.
AlSi10Mg tensile bars were additively manufactured using the powder-bed selective laser melting process. Samples were subjected to stress relief annealing and hot isostatic pressing. Tensile samples built using fresh, stored, and reused powder feedstock were characterized for microstructure, porosity, and mechanical properties. Fresh powder exhibited the best mechanical properties and lowest porosity while stored and reused powder exhibited inferior mechanical properties and higher porosity. The microstructure of stress relieved samples was fine and exhibited (001) texture in the z-build direction. Microstructure for hot isostatic pressed samples was coarsened with fainter (001) texture. To investigate surface and interior defects, scanning electron microscopy, optical fractography, and laser scanning microscopy techniques were employed. Hot isostatic pressing eliminated internal pores and reduced the size of surface porosity associated with the selective laser melting process. Hot isostatic pressing tended to increase ductility at the expense of decreasing strength. However, scatter in ductility of hot isostatic pressed parts suggests that the presence of unclosed surface porosity facilitated fracture with crack propagation inward from the surface of the part.
The powder-bed laser additive manufacturing (AM) process is widely used in the fabrication of three-dimensional metallic parts with intricate structures, where kinetically controlled diffusion and microstructure ripening can be hindered by fast melting and rapid solidification. Therefore, the microstructure and physical properties of parts made by this process will be significantly different from their counterparts produced by conventional methods. This work investigates the microstructure evolution for an AM fabricated AlSi10Mg part from its nonequilibrium state toward equilibrium state. Special attention is placed on silicon dissolution, precipitate formation, collapsing of a divorced eutectic cellular structure, and microstructure ripening in the thermal annealing process. These events alter the size, morphology, length scale, and distribution of the beta silicon phase in the primary aluminum, and changes associated with elastic properties and microhardness are reported. The relationship between residual stress and silicon dissolution due to changes in lattice spacing is also investigated and discussed.