Optimization of automated data collection is gaining increased interest for the purposes of enabling closed-loop self-correcting systems that inherently maximize operational efficiencies and reduce waste. Many data collection systems have several variables which influence data accuracy or consistency and which can require frequent user interaction to be monitored and maintained. Operating upon a Robo-MET.3D™ automated mechanical serial-sectioning system, a run-to-run control algorithm has been developed to accelerate data collection and reduce data inconsistency. Using historical data amassed over a decade of experiments, a linear regression model of the deterministic system dynamics is created and used to employ a run-to-run control algorithm that optimizes selected system inputs to reduce operator intervention and increase efficacy while reducing variance of system output.
Grain-scale microstructure evolution during additive manufacturing is a complex physical process. As with traditional solidification methods of material processing (e.g. casting and welding), microstructural properties are highly dependent on the solidification conditions involved. Additive manufacturing processes however, incorporate additional complexity such as remelting, and solid-state evolution caused by subsequent heat source passes and by holding the entire build at moderately high temperatures during a build. We present a three-dimensional model that simulates both solidification and solid-state evolution phenomena using stochastic Monte Carlo and Potts Monte Carlo methods. The model also incorporates a finite-difference based thermal conduction solver to create a fully integrated microstructural prediction tool. The three modeling methods and their coupling are described and demonstrated for a model study of laser powder-bed fusion of 300-series stainless steel. The investigation demonstrates a novel correlation between the mean number of remelting cycles experienced during a build, and the resulting columnar grain sizes.
The mechanical properties of additively manufactured metals tend to show high variability, due largely to the stochastic nature of defect formation during the printing process. This study seeks to understand how automated high throughput testing can be utilized to understand the variable nature of additively manufactured metals at different print conditions, and to allow for statistically meaningful analysis. This is demonstrated by analyzing how different processing parameters, including laser power, scan velocity, and scan pattern, influence the tensile behavior of additively manufactured stainless steel 316L utilizing a newly developed automated test methodology. Microstructural characterization through computed tomography and electron backscatter diffraction is used to understand some of the observed trends in mechanical behavior. Specifically, grain size and morphology are shown to depend on processing parameters and influence the observed mechanical behavior. In the current study, laser-powder bed fusion, also known as selective laser melting or direct metal laser sintering, is shown to produce 316L over a wide processing range without substantial detrimental effect on the tensile properties. Ultimate tensile strengths above 600 MPa, which are greater than that for typical wrought annealed 316L with similar grain sizes, and elongations to failure greater than 40% were observed. It is demonstrated that this process has little sensitivity to minor intentional or unintentional variations in laser velocity and power.
Porosity in additively manufactured metals can reduce material strength and is generally undesirable. Although studies have shown relationships between process parameters and porosity, monitoring strategies for defect detection and pore formation are still needed. In this paper, instantaneous anomalous conditions are detected in-situ via pyrometry during laser powder bed fusion additive manufacturing and correlated with voids observed using post-build micro-computed tomography. Large two-color pyrometry data sets were used to estimate instantaneous temperatures, melt pool orientations and aspect ratios. Machine learning algorithms were then applied to processed pyrometry data to detect outlier images and conditions. It is shown that melt pool outliers are good predictors of voids observed post-build. With this approach, real time process monitoring can be incorporated into systems to detect defect and void formation. Alternatively, using the methodology presented here, pyrometry data can be post processed for porosity assessment.
The third Sandia Fracture Challenge (SFC3) was a benchmark problem for comparing experimental and simulated ductile deformation and failure in an additively manufactured (AM) 316L stainless steel structure. One surprising observation from the SFC3 was the Challenge-geometry specimens had low variability in global load versus displacement behavior, attributed to the large stress-concentrating geometric features dominating the global behavior, rather than the AM voids that tend to significantly influence geometries with uniform cross-sections. This current study reinvestigates the damage and failure evolution of the Challenge-geometry specimens, utilizing interrupted tensile testing with micro-computed tomography (micro-CT) scans to monitor AM void and crack growth from a virgin state through complete failure. This study did not find a correlation between global load versus displacement behavior and AM void attributes, such as void volume, location, quantity, and relative size, which incidentally corroborates the observation from the SFC3. However, this study does show that the voids affect the local behavior of damage and failure. Surface defects (i.e. large voids located on the surface, far exceeding the nominal surface roughness) that were near the primary stress concentration affected the location of crack initiation in some cases, but they did not noticeably affect the global response. The fracture surfaces were a combination of classic ductile dimples and crack deviation from a more direct path favoring intersection with AM voids. Even though the AM voids promoted crack deviation, pre-test micro-CT scan statistics of the voids did not allow for conclusive predictions of preferred crack paths. This study is a first step towards investigating the importance of voids on the ductile failure of AM structures with stress concentrations.