Isothermal microcalorimetry (IMC) was used to better understand parasitic reactions and heat generation from Si electrodes in the first 10 cycles using Li/Si half cells. Heat generation from cell polarization (ohmic heat), entropy changes (reversible heat), and parasitic reactions (parasitic heat) are separated and quantified. The effect of temperature and fluoroethylene carbonate (FEC) as an electrolyte additive are also explored. Our results show that at the C/10 cycling rate used here, ohmic heat makes the largest contribution to overall heat generation while reversible heat is the smallest. Ohmic heat generation increases with cycle number due to increasing internal resistance, though the effect is smaller for cells with FEC. Interestingly, capacity-normalized parasitic heat generation is largely unaffected by changes in temperature despite differing reaction kinetics. We show that this is caused by a decrease in average parasitic reaction enthalpy as temperature is increased. Further, cells with FEC display higher average parasitic reaction enthalpy than cells without. The average parasitic reaction enthalpies for all the Si electrodes we tested were lower than previously reported values for graphite, indicating that the SEI formed on Si is less stable.
As we develop new materials to increase performance of lithium ion batteries for electric vehicles, the impact of potential safety and reliability issues become increasingly important. In addition to electrochemical performance increases (capacity, energy, cycle life, etc.), there are a variety of materials advancements that can be made to improve lithium-ion battery safety. Issues including energetic thermal runaway, electrolyte decomposition and flammability, anode SEI stability, and cell-level abuse tolerance behavior. Introduction of a next generation materials, such as silicon based anode, requires a full understanding of the abuse response and degradation mechanisms for these anodes. This work aims to understand the breakdown of these materials during abuse conditions in order to develop an inherently safe power source for our next generation electric vehicles.
Flow batteries are an attractive technology for energy storage of grid-scale renewables. However, performance issues related to ion-exchange membrane (IEM) fouling and crossover of species have limited the success of flow batteries. In this work we propose the use of the solid-state sodium-ion conductor NaSICON as an IEM to fully eliminate active species crossover in room temperature, aqueous, neutral pH flow batteries. We measure the room temperature conductivity of NaSICON at 2.83–4.67 mS cm−1 and demonstrate stability of NaSICON in an aqueous electrolyte with conductivity values remaining near 2.5 mS cm−1 after 66 days of exposure. Charge and discharge of a full H-cell battery as well as symmetric cycling in a flow battery configuration using NaSICON as an IEM in both cases demonstrates the capability of the solid-state IEM. Extensive analysis of aged cells through electrochemical impedance spectroscopy (EIS) and UV–vis spectroscopy show no contaminant species having crossed over the NaSICON membrane after 83 days of exposure, yielding an upper limit to the permeability of NaSICON of 4 × 10−10 cm2 min−1. The demonstration of NaSICON as an IEM enables a wide new range of chemistries for application to flow batteries that would previously be impeded by species crossover and associated degradation.
As we develop new materials to increase performance of lithium ion batteries for electric vehicles, the impact of potential safety and reliability issues become increasingly important. In addition to electrochemical performance increases (capacity, energy, cycle life, etc.), there are a variety of materials advancements that can be made to improve lithium-ion battery safety. Issues including energetic thermal runaway, electrolyte decomposition and flammability, anode SEI stability, and cell-level abuse tolerance behavior. Introduction of a next generation materials, such as silicon based anode, requires a full understanding of the abuse response and degradation mechanisms for these anodes. This work aims to understand the breakdown of these materials during abuse conditions in order to develop an inherently safe power source for our next generation electric vehicles. The effect of materials level changes (electrolytes, additives, silicon particle size, silicon loading, etc.) to cell level abuse response and runaway reactions will be determined using several techniques. Experimentation will start with base material evaluations in coin cells and overall runaway energy will be evaluated using techniques such as differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and accelerating rate calorimetry (ARC). The goal is to understand the effect of materials parameters on the runaway reactions, which can then be correlated to the response seen on larger cells (18650). Experiments conducted showed that there was significant response from these electrodes. Efforts to minimize risk during testing were taken by development of a smaller capacity cylindrical design in order to quantify materials decision and how they manifest during abuse response.
The objectives of this project are to elucidate degradation mechanisms, decomposition products, and abuse response for next generation silicon based anodes; and understand the contribution of various materials properties and cell build parameters towards thermal runaway enthalpies. Quantify the contributions from various cell parameters such as particle size, composition, state of charge (SOC), electrolyte to active materials ratio, etc.