The solution processability of ionogel solid electrolytes has recently garnered attention in the Li-ion battery community as a means to address the interface and fabrication issues commonly associated with most solid electrolytes. However, the trapped ionic liquid (ILE) component has hindered the electrochemical performance. In this report we present a process to tune the properties by replacing the ILE in a silica-based ionogel after fabrication with a liquid component befitting the desired application. Electrochemical cycling under various conditions showcases gels containing different liquid components incorporated into LiFePO4 (LFP)/gel/Li cells: high power (455 W kg–1 at a 1 C discharge) systems using carbonates, low temperatures (-40 °C) using ethers, or high temperatures (100 °C) using ionic liquids. Fabrication of additive-manufactured cells utilizing the exchanged carbonate-based system is demonstrated in a planar LFP/Li4Ti5O12 (LTO) system, where a marked improvement over an ionogel is found in terms of rate capability, capacity, and cycle stability (118 vs 41 mA h g–1 at C/4). This process represents a promising route to create a separator-less cell, potentially in complex architectures, where the electrolyte properties can be facilely tuned to meet the required conditions for a wide range of battery chemistries while maintaining a uniform electrolyte access throughout cast electrodes.
The development of chemistry is reported to implement selective dual-wavelength olefin metathesis polymerization for continuous additive manufacturing (AM). A resin formulation based on dicyclopentadiene is produced using a latent olefin metathesis catalyst, various photosensitizers (PSs) and photobase generators (PBGs) to achieve efficient initiation at one wavelength (e.g., blue light) and fast catalyst decomposition and polymerization deactivation at a second (e.g., UV-light). This process enables 2D stereolithographic (SLA) printing, either using photomasks or patterned, collimated light. Importantly, the same process is readily adapted for 3D continuous AM, with printing rates of 36 mm h–1 for patterned light and up to 180 mm h–1 using un-patterned, high intensity light.
Interest in 3D printing of thermoset resins has increased significantly in recent years. One approach to additive manufacturing of thermoset resins is printing dual-cure resins with direct ink write (DIW). Dual-cure resins are multi-component resins which employ an in situ curable constituent to enable net-shape fabrication while a second constituent and cure mechanism contribute to the final mechanical properties of the printed materials. In this work, the cure kinetics, green strength, printability, and print fidelity of dual-cure epoxy/acrylate thermoset resins are investigated. Resin properties are evaluated as a function of acrylate concentration and in situ UV exposure conditions. The acrylate cure kinetics are probed using photo-differential scanning calorimetry and the impacts of resin composition and UV cure profile on the acrylate extent of conversion are presented. Continuous and pulsed UV cure profiles are shown to affect total conversion due to variances in radical efficiency at different UV intensities and acrylate concentrations. The effects of acrylate concentration on the kinetics of the epoxy thermal cure and the final mechanical properties are also investigated using dynamic mechanical analysis and three-point bend measurements. The glass transition temperature is dependent on formulation, with increasing acrylate content decreasing the Tg. However, the room temperature shear moduli, flexural moduli, strength, strain-to-failure, and toughness values are relatively independent of resin composition. The similarity of the final properties allows for greater flexibility in resin formulation and in situ cure parameters, which can enable the printing of complex parts that require high green strength. We found that the in situ UV print intensities and exposure profiles that are necessary to achieve the best print quality are not, in most cases, the conditions that maximize conversion of the acrylate network. This highlights the importance of developing optimized resin compositions which enable complete cure of the acrylate network by promoting acrylate dark cure or thermal cure.
Additive Manufacturing (AM) of porous polymeric materials, such as foams, recently became a topic of intensive research due their unique combination of low density, impressive mechanical properties, and stress dissipation capabilities. Conventional methods for fabricating foams rely on complex and stochastic processes, making it challenging to achieve precise architectural control of structured porosity. In contrast, AM provides access to a wide range of printable materials, where precise spatial control over structured porosity can be modulated during the fabrication process enabling the production of foam replacement structures (FRS). Current approaches for designing FRS are based on intuitive understanding of their properties or an extensive number of finite element method (FEM) simulations. These approaches, however, are computationally expensive and time consuming. Therefore, in this work, we present a novel methodology for determining the mechanical compression response of direct ink write (DIW) 3D printed FRS using a simple cross-sectional image. By obtaining measurement data for a relatively small number of samples, an artificial neural network (ANN) was trained, and a computer vision algorithm was used to make inferences about foam compression characteristics from a single cross-sectional image. Finally, a genetic algorithm (GA) was used to solve the inverse design problem, generating the AM printing parameters that an engineer should use to achieve a desired compression response from a DIW printed FRS. The methods developed herein present an avenue for entirely autonomous design and analysis of additively manufactured structures using artificial intelligence.
The use of self-assembling, pre-polymer materials in 3D printing is rare, due to difficulties of facilitating printing with low molecular weight species and preserving their reactivity and/or functions on the macroscale. Akin to 3D printing of small molecules, examples of extrusion-based printing of pre-polymer thermosets are uncommon, arising from their limited rheological tuneability and slow reactions kinetics. The direct ink write (DIW) 3D printing of a two-part resin, Epon 828 and Jeffamine D230, using a self-assembly approach is reported. Through the addition of self-assembling, ureidopyrimidinone-modified Jeffamine D230 and nanoclay filler, suitable viscoelastic properties are obtained, enabling 3D printing of the epoxy–amine pre-polymer resin. A significant increase in viscosity is observed, with an infinite shear rate viscosity of approximately two orders of magnitude higher than control resins, in addition to, an increase in yield strength and thixotropic behavior. Printing of simple geometries is demonstrated with parts showing excellent interlayer adhesion, unachievable using control resins.
This SAND report fulfills the final report requirement for the Born Qualified Grand Challenge LDRD. Born Qualified was funded from FY16-FY18 with a total budget of ~$13M over the 3 years of funding. Overall 70+ staff, Post Docs, and students supported this project over its lifetime. The driver for Born Qualified was using Additive Manufacturing (AM) to change the qualification paradigm for low volume, high value, high consequence, complex parts that are common in high-risk industries such as ND, defense, energy, aerospace, and medical. AM offers the opportunity to transform design, manufacturing, and qualification with its unique capabilities. AM is a disruptive technology, allowing the capability to simultaneously create part and material while tightly controlling and monitoring the manufacturing process at the voxel level, with the inherent flexibility and agility in printing layer-by-layer. AM enables the possibility of measuring critical material and part parameters during manufacturing, thus changing the way we collect data, assess performance, and accept or qualify parts. It provides an opportunity to shift from the current iterative design-build-test qualification paradigm using traditional manufacturing processes to design-by-predictivity where requirements are addressed concurrently and rapidly. The new qualification paradigm driven by AM provides the opportunity to predict performance probabilistically, to optimally control the manufacturing process, and to implement accelerated cycles of learning. Exploiting these capabilities to realize a new uncertainty quantification-driven qualification that is rapid, flexible, and practical is the focus of this effort.
This report summarizes the data analysis activities that were performed under the Born Qualified Grand Challenge Project from 2016 - 2018. It is meant to document the characterization of additively manufactured parts and processe s for this project as well as demonstrate and identify further analyses and data science that could be done relating material processes to microstructure to properties to performance.
Plumley, John B.; Cook, Adam W.; Larsen, Christopher A.; Artyushkova, Kateryna; Han, Sang M.; Peng, Thomas L.; Kemp, Richard A.
Transparent electric conductors made of indium tin oxide (ITO)-doped glass prepared by a flash lamp annealing (FLA) process were compared with ITO-doped glass prepared via a conventional rapid thermal annealing (RTA) process. Stylus surface profilometry was used to determine thicknesses, scanning electron microscopy was used to image surfaces, X-ray diffraction was used to determine film structures, X-ray photoelectron spectroscopy was used to determine oxidation states and film compositions, 4-point probe measurements were used to determine electrical conductivities, UV–Vis spectroscopy was used to determine film transparencies, and selective light filtering was used to determine which wavelengths of light are needed to anneal ITO into a visibly transparent electrically conductive thin film via an FLA process. The results showed that FLA with visible light can be used to nearly instantaneously anneal ITO to create visibly transparent and electrically conductive ITO thin films on glass. The FLA process achieved this by predominately exciting unoxidized indium, unoxidized tin, tin monoxide (SnO), and non-stoichiometric indium oxide (InOx), appropriately distributed in an electron beam physical vapor-deposited amorphous ITO thin film, to allow their oxidation and crystallization into an electrically conductive visibly transparent ITO. Though it is possible to prepare ITO-doped glass that is more transparent with an RTA process, the FLA process is significantly faster, has comparable electrical conductivity, and can strongly localize heating to areas of the as-deposited ITO thin film that are not electrically conductive and visibly transparent.
Additive manufacturing offers unprecedented opportunities to design complex structures optimized for performance envelopes inaccessible under conventional manufacturing constraints. Additive processes also promote realization of engineered materials with microstructures and properties that are impossible via traditional synthesis techniques. Enthused by these capabilities, optimization design tools have experienced a recent revival. The current capabilities of additive processes and optimization tools are summarized briefly, while an emerging opportunity is discussed to achieve a holistic design paradigm whereby computational tools are integrated with stochastic process and material awareness to enable the concurrent optimization of design topologies, material constructs and fabrication processes.