Temperature-Dependent Friction and Wear Behavior of PTFE and MoS2

Babuska, Tomas F.; Pitenis, A.A.; Jones, M.R.; Nation, Brendan L.; Sawyer, W.G.; Argibay, Nicolas A.

An investigation of the temperature-dependent friction behavior of PTFE, MoS2, and PTFE-on-MoS2 is presented. Friction behavior was measured while continuously varying contact temperature in the range −150 to 175 °C while sliding in dry nitrogen, as well as for self-mated PTFE immersed in liquid nitrogen. These results contrast with previous reports of high-friction transitions and plateaus for pure and composite MoS2 at temperatures below about −20 °C; instead, we have found persistently weak thermal behavior between 0 and −196 °C, providing new insight about the molecular mechanisms of macroscale friction. The temperature-dependent friction behavior characteristic of self-mated PTFE was found also for PTFE-on-MoS2 sliding contacts, suggesting that PTFE friction was defined by subsurface deformation mechanisms and internal friction even when sliding against a lamellar lubricant with extremely low friction coefficient (µ ~ 0.02). The various relaxation temperatures of PTFE were found in the temperature-dependent friction behavior, showing excellent agreement with reported values acquired using rheological techniques measuring energy dissipation through internal friction. Additionally, hysteresis in friction behavior suggests an increase in near-surface crystallinity upon exceeding the high-temperature relaxation, Tα ~ 116 °C.