Synthesis of magnesiowüstite nanocrystallites embedded in an amorphous silicate matrix via low energy multiple ion implantations

Young, Joshua M.; Byers, Todd A.; Lang, Eric J.; Singh, Satyabrata; Glass, Gary A.; Hattar, Khalid M.; Rout, Bibhudutta

A synthesis process is presented for experimentally simulating modifications in cosmic dust grains using sequential ion implantations or irradiations followed by thermal annealing. Cosmic silicate dust analogues were prepared via implantation of 20–80 ​keV Fe−, Mg−, and O− ions into commercially available p-type silicon (100) wafers. The as-implanted analogues are amorphous with a Mg/(Fe ​+ ​Mg) ratio of 0.5 tailored to match theoretical abundances in circumstellar dusts. Before the ion implantations were performed, Monte-Carlo-based ion-solid interaction codes were used to model the dynamic redistribution of the implanted atoms in the silicon substrate. 600 ​keV helium ion irradiation was performed on one of the samples before thermal annealing. Two samples were thermally annealed at a temperature appropriate for an M-class stellar wind, 1000 ​K, for 8.3 ​h in a vacuum chamber with a pressure of 1 ​× ​10−7 torr. The elemental depth profiles were extracted utilizing Rutherford Backscattering Spectrometry (RBS) in the samples before and after thermal annealing. X-ray diffraction (XRD) analysis was employed for the identification of various phases in crystalline minerals in the annealed analogues. Transmission electron microscopy (TEM) analysis was utilized to identify specific crystal structures. RBS analysis shows redistribution of the implanted Fe, Mg, and O after thermal annealing due to incorporation into the crystal structures for each sample type. XRD patterns along with TEM analysis showed nanocrystalline Mg and Fe oxides with possible incorporation of additional silicate minerals.