Solid state bonding of CuCrZr to 316L stainless steel for ITER applications

Goods, Steven H.; Puskar, J.D.

Dissimilar metal bonds between CuCrZr and 316L stainless steel were prepared using two different solid state joining techniques. In the first instance, hot isostatic pressing, a high temperature diffusion bonding process was used to join the copper alloy to the stainless steel substrate at temperatures near 1000 °C. In the second instance, explosion bonding at ambient temperature was employed. These two techniques both yielded mechanically robust joints, where the strength of the interface exceeded that of the copper alloy, the weaker of the two substrates. However, the two bonding techniques produced near-joint microstructures that were very different. The microstructure and mechanical performance of CuCrZr/316L stainless steel joints prepared via both techniques are compared. Microstructural analysis of the joints included scanning electron microscopy, electron microprobe analysis and Auger spectroscopy techniques. The bulk mechanical properties of the substrate alloys were very different as well and are described. Particular emphasis is placed on the residual mechanical properties of the CuCrZr after thermal processing that simulate beryllium tile bonding since once the Be tiles are in place, the copper alloy cannot be solutionized and age-hardened to return it to full strength. © 2010 Elsevier B.V. All rights reserved.