Publications
Solid oxide fuel cell electrolytes produced by a combination of suspension plasma spray and very low pressure plasma spray
Plasma spray coating techniques allow unique control of electrolyte microstructures and properties as well as facilitating deposition on complex surfaces. This can enable significantly improved solid oxide fuel cells (SOFCs), including non-planar designs. SOFCs are promising because they directly convert the oxidization of fuel into electrical energy. However, electrolytes deposited using conventional plasma spray are porous and often greater than 50 microns thick. One solution to form dense, thin electrolytes of ideal composition for SOFCs is to combine suspension plasma spray (SPS) with very low pressure plasma spray (VLPPS). Increased compositional control is achieved due to dissolved dopant compounds in the suspension that are incorporated into the coating during plasma spraying. Thus, it is possible to change the chemistry of the feed stock during deposition. In the work reported, suspensions of sub-micron diameter 8 mol.% Y2O3-ZrO2 (YSZ) powders were sprayed on NiO-YSZ anodes at Sandia National Laboratories (SNL) Thermal Spray Research Laboratory (TSRL). These coatings were compared to the same suspensions doped with scandium nitrate at 3 to 8 mol%. The pressure in the chamber was 2.4 torr and the plasma was formed from a combination of argon and hydrogen gases. The resultant electrolytes were well adhered to the anode substrates and were approximately 10 microns thick. The microstructure of the resultant electrolytes will be reported as well as the electrolyte performance as part of a SOFC system via potentiodynamic testing and impedance spectroscopy.