Self-Cleaning Synthetic Adhesive Surfaces Mimicking Tokay Geckos

Branson, Eric D.; Singh, Seema S.; Burckel, David B.; Fan, Hongyou F.; Houston, Jack E.; Brinker, C.J.

A gecko's extraordinary ability to suspend itself from walls and ceilings of varied surface roughness has interested humans for hundreds of years. Many theories and possible explanations describing this phenomenon have been proposed including sticky secretions, microsuckers, and electrostatic forces; however, today it is widely accepted that van der Waals forces play the most important role in this type of dry adhesion. Inarguably, the vital feature that allows a gecko's suspension is the presence of billions 3 of tiny hairs on the pad of its foot called spatula. These features are small enough to reach within van der Waals distances of any surface (spatula radius %7E100 nm); thus, the combined effect of billions of van der Waals interactions is more than sufficient to hold a gecko's weight to surfaces such as smooth ceilings or wet glass. Two lithographic approaches were used to make hierarchal structures with dimensions similar to the gecko foot dimensions noted above. One approach combined photo-lithography with soft lithography (micro-molding). In this fabrication scheme the fiber feature size, defined by the alumina micromold was 0.2 um in diameter and 60 um in height. The second approach followed more conventional photolithography-based patterning. Patterned features with dimensions %7E0.3 mm in diameter by 0.5 mm tall were produced. We used interfacial force microscopy employing a parabolic diamond tip with a diameter of 200 nm to measure the surface adhesion of these structures. The measured adhesive forces ranged from 0.3 uN - 0.6 uN, yielding an average bonding stress between 50 N/cm2 to 100 N/cm2. By comparison the reported literature value for the average stress of a Tokay gecko foot is 10 N/cm2. Acknowledgements This work was funded by Sandia National Laboratory's Laboratory Directed Research & Development program (LDRD). All coating processes were conducted in the cleanroom facility located at the University of New Mexico's Center for High Technology Materials (CHTM). SEM images were performed at UNM's Center for Micro-Engineering on equipment funded by a NSF New Mexico EPSCoR grant. 4