Yarrington, Cole Y.; Abere, Michael J.; Adams, David P.; Hobbs, Michael L.

Al/Pt nanolaminates with a bilayer thickness (tb, width of an Al/Pt pair-layer) of 164 nm were irradiated with single laser pulses with durations of 10 ms and 0.5 ms at 189 W/cm2 and 1189 W/cm2, respectively. The time to ignition was measured for each pulse, and shorter ignition times were observed for the higher power/shorter pulse width. Videographic images of the irradiated area shortly after ignition show a non-uniform radial brightness for the longer pulse, while the shorter pulse shows uniform brightness. A diffusion-limited single step reaction mechanism was implemented in a finite element package to model the progress from reactants to products at both pulse widths. The model captures well both the observed ignition delay and qualitative observations regarding the non-uniform radial temperature.