Radiation Testing of a Low Voltage Silicone Nuclear Power Plant Cable

White II, Gregory V.; Schroeder, John L.; Sawyer, P.S.; Wichhart, Derek W.; Mata, Guillermo A.; Zorrilla, Jorge Z.; Bernstein, Robert B.

This report summarizes the results generated in FY13 for cable insulation in support of the Department of Energy's Light Water Reactor Sustainability (LWRS) Program, in collaboration with the US-Argentine Binational Energy Working Group (BEWG). A silicone (SiR) cable, which was stored in benign conditions for %7E30 years, was obtained from Comision Nacional de Energia Atomica (CNEA) in Argentina with the approval of NA-SA (Nucleoelectrica Argentina Sociedad Anonima). Physical property testing was performed on the as-received cable. This cable was artificially aged to assess behavior with additional analysis. SNL observed appreciable tensile elongation values for all cable insulations received, indicative of good mechanical performance. Of particular note, the work presented here provides correlations between measured tensile elongation and other physical properties that may be potentially leveraged as a form of condition monitoring (CM) for actual service cables. It is recognized at this point that the polymer aging community is still lacking the number and types of field returned materials that are desired, but Sandia National Laboratories (SNL) -- along with the help of others -- is continuing to work towards that goal. This work is an initial study that should be complimented with location-mapping of environmental conditions of Argentinean plant conditions (dose and temperature) as well as retrieval, analysis, and comparison with in- service cables.