Processing of Silicon Nitride Ceramics from Concentrated Aqueous Suspensions by Robocasting

Cesarano, Joseph C.; Stuecker, John N.; Cesarano, Joseph C.

The optimization of concentrated AlliedSignal GS-44 silicon nitride aqueous slurries for robocasting was investigated. The dispersion mechanisms of GS-44 Si{sub 3}N{sub 4} aqueous suspensions with and without polyacrylate were analyzed. The zero point of charge (ZPC) was at about pH 6. Well-dispersed GS-44 suspensions were obtained in the pH range from 7 to 11 by the addition of Darvan 821A. The influence of pH, amount of Darvan 821A and solids loading on the theological behavior of GS-44 aqueous suspensions was determined. A coagulant, aluminum nitrate, was used to control the yield stress and shear thinning behavior of highly loaded Si{sub 3}N{sub 4} slurries. Homogeneous and stable suspensions of 52 vol% GS-44 Si{sub 3}N{sub 4} were robocast successfully at pH 7.8 to pH 8.5. The sintering process, mechanical properties and microstructural characteristics of robocast GS-44 bars were determined.