Molecular-To-Continuum Fracture Analysis of Thermosetting Polymer/Solid Interfaces

Kent, Michael S.; Reedy, Earl D.; Stevens, Mark J.

This report focuses on the relationship between the fundamental interactions acting across an interface and macroscopic engineering observable such as fracture toughness or fracture stress. The work encompasses experiment, theory, and simulation. The model experimental system is epoxy on polished silicon. The interfacial interactions between the substrate and the adhesive are varied continuously using self-assembling monolayer. Fracture is studied in two specimen geometries: a napkin-ring torsion geometry and a double cantilevered beam specimen. Analysis and modeling involves molecular dynamics simulations and continuum mechanics calculations. Further insight is gained from analysis of measurements in the literature of direct force measurements for various fundamental interactions. In the napkin-ring test, the data indicate a nonlinear relationship between interface strength and fracture stress. In particular, there is an abrupt transition in fracture stress which corresponds to an adhesive-to-cohesive transition. Such nonlinearity is not present in the MD simulations on the tens-of-nanometer scale, which suggests that the nonlinearity comes from bulk material deformation occurring on much larger length scales. We postulate that the transition occurs when the interface strength becomes comparable to the yield stress of the material. This postulate is supported by variation observed in the fracture stress curve with test temperature. Detailed modeling of the stress within the sample has not yet been attempted. In the DCB test, the relationship between interface strength and fracture toughness is also nonlinear, but the fracture mechanisms are quite different. The fracture does not transition from adhesive to cohesive, but remains adhesive over the entire range of interface strength. This specimen is modeled quantitatively by combining (i) continuum calculations relating fracture toughness to the stress at 90 {angstrom} from the crack tip, and (ii) a relationship from molecular simulations between fracture stress on a {approx} 90 {angstrom} scale and the fraction of surface sites which chemically bond. The resulting relationship between G{sub c} and fraction of bonding sites is then compared to the experimental data. This first order model captures the nonlinearity in the experimentally-determined relationship. A much more extensive comparison is needed (calculations extending to higher G{sub c} values, experimental data extending to lower G{sub c} values) to guide further model development.