LiF dissolution by anion-binding-agent in LiCFx battery systems: Lower ohmic and interfacial resistance
Nagasubramanian, Ganesan N.; Fenton, Kyle R.
In this paper we will discuss our preliminary thermal and electrochemical data aimed at developing a robust nonflammable Li-CFx cell capable of wide temperature operation. To accomplish this goal, we are evaluating a thermally stable solvent comprised of an anion binding agent (ABA) and lithium fluoride (LiF), typically at a 1:1 molar ratio. In conventional carbonate based electrolytes, ABA is soluble while LiF remains insoluble. However, the neutral ABA solubilizes LiF and forms a salt complex represented as Li+(ABAF-). We are exploiting this unique feature and apply this strategy to CFx chemistry to improve cell performance, due to the CFx cell chemistry generating LiF as discharge product. Continuous solvation of the salt mixture during discharge allows for utilization of electrolytes initially containing sub stoichiometric amount of LiF. The practical benefits are reduced cell weight, mitigation of electrode fouling, and consequently better low temperature performance. Electrolytes containing dimethyl methyl phosphonate (DMMP), 1M tris(pentafluorophenyl) borane (TPFB) and varying concentrations of LiF (1M; 0.5M and 0.1M) were prepared and characterized for ionic conductivity and voltage stability. In general, ionic conductivity decreases with decreasing LiF concentration. The room temperature conductivity for the DMMP 1M TPFB:1M LiF is ~ 9mS/cm and ~3mS/cm for the 1M TPFB:0.1M LiF. Unlike the conductivity, the electrochemical voltage stability did not vary substantially with LiF concentration and the electrolytes showed a stable voltage window in the range 0-3.5V vs. Li+/Li, which is substantially wider than the Li-CFx cell voltage. Flammability measurement performed at our thermal abuse facility demonstrated that the electrolyte was nonflammable. Discharge performance of CFx materials obtained from several vendors was evaluated in 2032 coin cells at room temperature. Experimental results demonstrate a reduction in ohmic resistance and interfacial resistance during discharge for a cell containing lower concentrations of added LiF compared to ABA. These observations are a direct demonstration that the unbound ABA in the electrolyte dissolves the LiF generated in the discharge reaction.