Issues associated with the metalorganic chemical vapor deposition of ScGaN and YGaN alloys

Koleske, Daniel K.; Creighton, J.R.; Crawford, Mary H.; Cross, Karen C.; Knapp, J.A.

The most energy efficient solid state white light source will likely be a combination of individually efficient red, green, and blue LED. For any multi-color approach to be successful the efficiency of deep green LEDs must be significantly improved. While traditional approaches to improve InGaN materials have yielded incremental success, we proposed a novel approach using group IIIA and IIIB nitride semiconductors to produce efficient green and high wavelength LEDs. To obtain longer wavelength LEDs in the nitrides, we attempted to combine scandium (Sc) and yttrium (Y) with gallium (Ga) to produce ScGaN and YGaN for the quantum well (QW) active regions. Based on linear extrapolation of the proposed bandgaps of ScN (2.15 eV), YN (0.8 eV) and GaN (3.4 eV), we expected that LEDs could be fabricated from the UV (410 nm) to the IR (1600 nm), and therefore cover all visible wavelengths. The growth of these novel alloys potentially provided several advantages over the more traditional InGaN QW regions including: higher growth temperatures more compatible with GaN growth, closer lattice matching to GaN, and reduced phase separation than is commonly observed in InGaN growth. One drawback to using ScGaN and YGaN films as the active regions in LEDs is that little research has been conducted on their growth, specifically, are there metalorganic precursors that are suitable for growth, are the bandgaps direct or indirect, can the materials be grown directly on GaN with a minimal defect formation, as well as other issues related to growth. The major impediment to the growth of ScGaN and YGaN alloys was the low volatility of metalorganic precursors. Despite this impediment some progress was made in incorporation of Sc and Y into GaN which is detailed in this report. Primarily, we were able to incorporate up to 5 x 10{sup 18} cm{sup -3} Y atoms into a GaN film, which are far below the alloy concentrations needed to evaluate the YGaN optical properties. After a no-cost extension was granted on this program, an additional more 'liquid-like' Sc precursor was evaluated and the nitridation of Sc metals on GaN were investigated. Using the Sc precursor, dopant level quantities of Sc were incorporated into GaN, thereby concluding the growth of ScGaN and YGaN films. Our remaining time during the no-cost extension was focused on pulsed laser deposition of Sc metal films on GaN, followed by nitridation in the MOCVD reactor to form ScN. Finally, GaN films were deposited on the ScN thin films in order to study possible GaN dislocation reduction.