Influence of Al location on formation of silver clusters in mordenite

Rimsza, Jessica R.; Chapman, Karena W.; Nenoff, T.M.

Formation of zeolite supported Ag0 clusters depends on a combination of thermodynamically stable atomic configurations, charge balance considerations, and mobility of species on the surface and within pores. Periodic density functional theory (DFT) calculations were performed to evaluate how the location of Al in the mordenite (MOR) framework and humidity control Ag0 nanocluster formation. Four Al framework sites were studied (T1-T4) and the Al positions in the framework were identified by the shifts in the differential Al⋯Al pair distribution function (PDF). Furthermore, structural information about the Ag0 nanoclusters, such as dangling bonds, can be identified by Ag⋯Ag PDF data. For Ag0 formation in vacuum MOR structures with a Si:Al ratio of 5:1 with Al in the T1 position resulted in the most framework flexibility and the lowest Ag0 nanocluster charge, indicating the best result for formation of charge neutral nanoclusters. When water is present, Al in the T3 and T4 positions results in the formation of the smallest average Ag0 nanoclusters plus greater expansion of the O-T-O bond angle than in vacuum, indicating easier diffusion of the Ag0 nanoclusters to the surface. The presence of Al in 4-membered rings and in pairs indicates favorable MOR structures for formation of single Ag atoms, despite the existence of synthesis challenges. Therefore, Al in the T2 position is the least favorable for Ag0 nanocluster formation in both vacuum and in the presence of water. Al in the T1, T3, and T4 positions provides beneficial effects through framework flexibility and changes in nanocluster size or charge that can be leveraged for design of zeolites for formation of metallic nanoclusters.