Incipient Melting in AA7075

Brehm, Johnathon R.; Buckner, Jessica L.; Profazi, Christina A.; Hickman, Renae E.

Incipient melting is a phenomenon that can occur in aluminum alloys where solute rich areas, such as grain boundaries, can melt before the rest of the material; incipient melting can degrade mechanical and corrosion properties and is irreversible, resulting in material scrapping. After detecting indications of incipient melting as the cause of failure in 7075 aluminum alloy parts (AA7075), a study was launched to determine threshold temperature for incipient melting. Samples of AA7075 were solution annealed using temperatures ranging from 870-1090F. A hardness profile was developed to demonstrate the loss of mechanical properties through the progression of incipient melting. Additionally, Zeiss software Zen Core Intellesis was utilized to more accurately quantify the changes in microstructural properties as AA7075 surpassed the onset of incipient melting. The results from this study were compared with previous AA7075 material that demonstrated incipient melting.