In-situ time-of-flight neutron diffraction of ErD2 (beta phase) formation during D2 loading

Rodriguez, Marko A.; Snow, Clark S.; Wixom, Ryan R.

In an effort to better understand the structural changes occurring during hydrogen loading of erbium target materials, we have performed D{sub 2} loading of erbium metal (powder) with simultaneous neutron diffraction analysis. This experiment tracked the conversion of Er metal to the {alpha} erbium deuteride (solid-solution) phase and then on to the {beta} (fluorite) phase. Complete conversion to ErD{sub 2.0} was accomplished at 10 Torr D{sub 2} pressure with deuterium fully occupying the tetrahedral sites in the fluorite lattice. Increased D{sub 2} pressure (up to 500 Torr at 450 C) revealed {approx}10 % deuterium occupation of the octahedral sites. Subsequent vacuum pumping of the sample at 450 C removed octahedral site occupancy while maintaining tetrahedral deuterium occupancy, thereby yielding stoichiometric ErD{sub 2.0} {beta} phase.