In situ tem observations of corrosion in nanocrystalline fe thin films

Gross, David; Kacher, Josh; Key, Jordan; Hattar, Khalid M.; Robertson, Ian M.

The corrosion of pulsed-laser deposited Fe thin films by aqueous acetic acid solution was explored in real time by performing dynamic microfluidic experiments in situ in a transmission electron microscope. The films were examined in both the as-deposited condition and after annealing. In the as-deposited films, discrete events featuring the localized dissolution of grains were observed with the dissolved volumes ranging in size from ~1.5 x 10-5 μm3 to 3.4 x 10-7 μm3. The annealed samples had larger grains than the as-deposited samples, were more resistant to corrosion, and did not show similar discrete dissolution events. The electron beam was observed to accelerate the corrosion, especially on the as-deposited samples. The effects of grain surface energy, grain boundary energy and the electron beam-specimen interactions are discussed in relation to the observed behavior.