Improved rubber nanofillers
During this task, Silane functionalized TiO2 and HK3Ti4O4(SiO4)3 were sent to Goodyear (GY) for testing. These materials were characterized based on their interaction with the model elastomer, squalene. The Van der Waals interactions and Hamaker Constants for ZnO particles in squalene and rubber materials were characterized and it was determined that a 10-20 nm spacing was necessary between primary filler particles to maintain a stable nanocomposite. Contact angle measurements on the ZnO and ZnO-silane materials indicated that the solvent should wet the particles, and solvophobic attractions should not be present. These studies showed that the surface modification with sulfosilane coupling agents was successful, and high levels of dispersion of the particles remained possible. Further, a novel surface charging phenomenon where negative surface charging is developed in the squalene environment was observed and corroborated by measurements of particle size and of the surface modified materials in squalene. This impacts the dispersion of the particles according to the traditional colloidal interpretation of electrostatic repulsive forces between particles. Additionally, thin nanocomposite fibers were developed using electrospinning. The size and shape of the oxides did not change during the electrospinning process, although the shape of the fiber and the distribution of the particles, particularly for ZnO, was not ideal. There was an obvious increase in elastic modulus and hardness from the addition of the oxides, but differentiating the oxides, and particularly the surfactants, was difficult. The A-1289 lead to the greatest dispersion of the filler particles, while the A-1589 and the NXT produced clustered particle aggregates. This agrees with previous study of these materials in low molecular weight squalene solvent studies reported earlier. The behavior of the nanoparticle ZnO and the microparticle silica is different as well, with the ZnO being contained within the elastomer, and the SiO2 forming monolayers at the surface of the elastomer. The dynamic mechanical analysis did not show clear trends between the surface modification and the aggregate structure. In the silica particles, the NXT led to the least particle interaction, followed by the A-1289 and highest particle interaction found for the A-1589. For the nanosized ZnO, the best dispersion was found for the A-1589, with both the A-1289 and NXT exhibiting frequency dependent responses.