High temperature operation to 500 °c of AlGaN graded polarization-doped field-effect transistors

Carey, Patrick H.; Ren, Fan; Armstrong, Andrew A.; Klein, Brianna A.; Allerman, A.A.; Douglas, Erica A.; Baca, A.G.; Pearton, Stephen J.

AlGaN polarization-doped field-effect transistors were characterized by DC and pulsed measurements from room temperature to 500 °C in ambient. DC current-voltage characteristics demonstrated only a 70% reduction in on-state current from 25 to 500 °C and full gate modulation, regardless of the operating temperature. Near ideal gate lag measurement was realized across the temperature range that is indicative of a high-quality substrate and sufficient surface passivation. The ability for operation at high temperature is enabled by the high Schottky barrier height from the Ni/Au gate contact, with values of 2.05 and 2.76 eV at 25 and 500 °C, respectively. The high barrier height due to the insulatorlike aluminum nitride layer leads to an ION/IOFF ratio of 1.5 × 109 and 6 × 103 at room temperature and 500 °C, respectively. Transmission electron microscopy was used to confirm the stability of the heterostructure even after an extended high-temperature operation with only minor interdiffusion of the Ni/Au Schottky contact. The use of refractory metals in all contacts will be key to ensure a stable extended high-temperature operation.