Gas Gun Impact Testing of PZT 95/5, Part 1: Unpoled State

Furnish, Michael D.; Setchell, Robert E.; Chhabildas, Lalit C.; Montgomery, Stephen M.

In the present study, 10 impact tests were conducted on unpoled PZT 95/5, with 9% porosity and 2 at% Nb doping. These tests were instrumented to obtain time-resolved loading, unloading and span signatures. As well, PVDF gauges allowed shock timing to be established explicitly. The ferroelectric/antiferroelectric phases transition was manifested as a ramp to 0.4 GPa. The onset of crushup produced the most visible signature: a clear wave separation at 2.2 GPa followed by a highly dispersive wave. The end states also reflected crushup, and are consistent with earlier data and with related poled experiments. A span strength value of 0.17 GPa was measured for a shock stress of 0.5 GPa, this decreased to a very small value (no visible pullback signature) for a shock strength of 1.85 GPa.