Fire-Induced Pressure Response and Failure Characterization of PCV/SCV/3013 Containers - Phase 3

Mendoza, Hector M.; Baird, Austin R.; Gill, Walt; Figueroa Faria, Victor G.; McClard, James M.; Sprankle, Ray S.; Hensel, Steve H.; Michel, Danielle M.; Adee, Shane M.

Several Department of Energy (DOE) facilities have materials stored in robust, welded, stainless - steel containers with presumed fire - induced pressure response behaviors. Lack of test data related to fire exposure requires conservative safety analysis assumptions for container response at these facilities. This conservatism can in turn result in the implementation of challenging operational restrictions with costly nuclear safety controls. To help address this issue for sites that store DOE 3013 stainless - steel containers, a series of ten tests were undertaken at Sandia National Laboratories. The goal of this test series was to obtain the response behavior for various configurations of DOE 3013 containers with various payload compositions when exposed to one of two ASTM fire conditions. Key parameters measured in the test series included identification of failure - specific characteristics such as pressure, temperature, and whether or not a vessel was breached during a test . Numerous failure - specific characteristics were identified from the ten tests. This report describes the implementation and execution of the test series performed to identify these failure - specific characteristics. Discussions on the test configurations, payload compositions, thermal insults, and experimental setups are presented. Test results in terms of pressurization and vessel breach (or no - breach) are presented along with corresponding discussions for each test.