Fatigue stress concentration and notch sensitivity in nanocrystalline metals

Furnish, Timothy A.; Boyce, Brad B.; Sharon, John A.; O'Brien, Christopher J.; Clark, Blythe C.; Arrington, Christian L.; Pillars, Jamin R.

Recent studies have shown the potential for nanocrystalline metals to possess excellent fatigue resistance compared to their coarse-grained counterparts. Although the mechanical properties of nanocrystalline metals are believed to be particularly susceptible to material defects, a systematic study of the effects of geometric discontinuities on their fatigue performance has not yet been performed. In the present work, nanocrystalline Ni-40 wt%Fe containing both intrinsic and extrinsic defects were tested in tension-tension fatigue. The defects were found to dramatically reduce the fatigue resistance, which was attributed to the relatively high notch sensitivity in the nanocrystalline material. Microstructural analysis within the crack-initiation zones underneath the defects revealed cyclically-induced abnormal grain growth (AGG) as a predominant deformation and crack initiation mechanism during high-cycle fatigue. The onset of AGG and the ensuing fracture is likely accelerated by the stress concentrations, resulting in the reduced fatigue resistance compared to the relatively defect-free counterparts.