Cold Spray of C22Gd Coatings for Nuclear Waste Storage

Mahaffey, Jacob T.; Padilla, Joseph A.

C22-Gd films were deposited onto 316 stainless steel up to 2.4mm thick using three different cold spray conditions. No differences in visible coating adhesion was observed between grit-blasted and as-received 316 stainless steel substrates. All of the coatings produced had a density greater than 95% of bulk. EDS and backscattered imaging suggest that no secondary phases precipitated during coating fabrication, but potential micro-segregation of phases were likely present in the as-received material. The phase segregation was still observable in the as-deposited coatings. EDS could not resolve the differences in composition of the two phases.