Characterization of Water and CO2 Adsorption by Stores 3A Desiccant Samples Using Thermal Gravimetric Analysis and Fourier Transform Infrared Spectroscopy

Rivera, Dion A.; Rivera, Dion A.; Alam, Mary K.; Brown, Jason R.

Two lots of manufactured Type 3a zeolite samples were compared by TGA/IR analysis. The first lot, obtained from Davidson Chemical, a commercial vendor, was characterized during the previous study cycle for its water and water-plus-CO{sub 2} uptake in order to determine whether CO{sub 2} uptake prevented water adsorption by the zeolite. It was determined that CO{sub 2} did not hamper water adsorption using the Davidson zeolite. CO{sub 2} was found on the zeolite surface at dewpoints below -40 C, however it was found to be reversibly adsorbed. During the course of the previous studies, chemical analyses revealed that the Davidson 3a zeolite contained calcium in significant quantities, along with the traditional counterions potassium and sodium. Chemical analysis of a Type 3a zeolite sample retrieved from Kansas City (heretofore referred to as the ''Stores 3a'' sample) indicated that the Stores sample was a more traditional Type 3a zeolite, containing no calcium. TGA/IR studies this year focused on obtaining CO{sub 2} and water absorbance data from the Stores 3a zeolite. Within the Stores 3a sample, CO{sub 2} was found to be reversibly absorbed within the sample, but only at and below -60 C with 5% CO{sub 2} loading. The amount of CO{sub 2} observed eluting from the Stores zeolite at this condition was similar to what was observed from the Davidson zeolite sample but with a greater uncertainty in the measured value. The results of the Stores 3a studies are summarized within this report.