Al0_0.3Ga_0.7N PN diode with breakdown voltage >1600 V

Allerman, A.A.; Armstrong, Andrew A.; Fischer, Arthur J.; Dickerson, Jeramy R.; Crawford, Mary H.; King, Michael P.; Moseley, Michael; Wierer, J.Jr.; Kaplar, Robert K.

Demonstration of Al0_0.3Ga_0.7N PN diodes grown with breakdown voltages in excess of 1600 V is reported. The total epilayer thickness is 9.1 μm and was grown by metal-organic vapour-phase epitaxy on 1.3-mm-thick sapphire in order to achieve crack-free structures. A junction termination edge structure was employed to control the lateral electric fields. A current density of 3.5 kA/cm² was achieved under DC forward bias and a reverse leakage current <3 nA was measured for voltages <1200 V. The differential on-resistance of 16 mΩ cm² is limited by the lateral conductivity of the n-type contact layer required by the front-surface contact geometry of the device. An effective critical electric field of 5.9 MV/cm was determined from the epilayer properties and the reverse current–voltage characteristics. To our knowledge, this is the first aluminium gallium nitride (AlGaN)-based PN diode exhibiting a breakdown voltage in excess of 1 kV. Finally, we note that a Baliga figure of merit (V_br²/R_spec,on) of 150 MW/cm² found is the highest reported for an AlGaN PN diode and illustrates the potential of larger-bandgap AlGaN alloys for high-voltage devices.