bulk modulus at 23C:
from dilatometer = 4.92 GPa
KIC from pre-cracked 3-pt bend samples at 23C = 0.66 MPa-m1/2
stress at failure from stainless steel napkin ring at 23C
= 52.7 ± 2.7 MPa